【摘 要】
：
To gain insight into the ageing behavior of ultrafine grain(UFG)structure,the precipitation phenom-ena and microstructural evolutions of Mg-6Zn-1Y-0.4Ce-0.5 Zr(
【机 构】
：
International Joint Laboratory for Light Alloys(MOE),College of Materials Science and Engineering,Ch
论文部分内容阅读
To gain insight into the ageing behavior of ultrafine grain(UFG)structure,the precipitation phenom-ena and microstructural evolutions of Mg-6Zn-1Y-0.4Ce-0.5 Zr(wt.％)alloy processed by sliding friction treatment(SFT)were systematically studied using hardness texting,transmission electron microscopy(TEM)equipped with high-angle annular dark-field scanning(HADDF-STEM),X-ray diffraction(XRD)and XRD line broadening analysis.The microhardness of the SFT-processed(SFTed)sample initially decreases from 109.6 HV to 104.8 HV at ageing for 8 h,and then increases to the peak-ageing point of 115.4 HV at 16 h.Subsequently,it enters the over-aged period.The un-SFTed sample,as the counterpart,follows a regular ageing behavior that increases from 89.9 HV to 99.6 HV when ageing for 12 h,and then drops.A multi-mechanistic model is established to describe the strengthening due to grain refinement,disloca-tion accumulation,precipitation etc.The analysis reveals that the temperature sensitive UFG structure has an obvious grain coarsening effect,which arouses the soft phenomenon in the early ageing stage.But precipitation hardening provides an excellent hardness enhancement for overcoming the negative influ-ence and helping to reach the peak-aged point.In our microstructural observations,a lot of equilibrium ultrafine MgZn2 precipitates precipitate along dislocations because defects can provide the favorable conditions for the migration and segregation of solute atoms.
其他文献
The effect of a high magnetic field on the microstructural evolution of a peritectic Al-18 at.％Ni alloy during directional solidification and its dependence on p
A nanocrystalline CoCrFeNiMn high-entropy alloy(nc-HEA)with nano-multiphase structure was pre-pared by inert gas condensation(IGC)using a laser evaporation sour
A novel equimolar high-entropy(HE)transition metal monoboride,(Cr0.2Mn0.2Fe0.2Co0.2Mo0.2)B,was designed and prepared in powder and bulk form by high temperature
The undercooling dependence of the solidification mechanism was systematically explored by the elec-trostatic levitation(ESL)facility.During the experiments,the
Laser aided additive manufacturing(LAAM)was used to fabricate bulk Fe49.5Mn30Co10Cr10C0.5 interstitial multicomponent alloy using pre-alloyed powder.The room te
The synergistic effects of area ratio and microstructure on the galvanic corrosion of A508/309 L/308 L dissimilar metals weld(DMW)are studied by a multi-analytical approach.It was demonstrated that decreasing the anode/cathode surface area ratio obviously
Construction of metal-organic-frameworks-based composite photocatalysts has attracted much atten-tion for the reasonable band gap and high surface areas to impr
2D transition metal dichalcogenides(TMDs)have been considered as promising non-precious electrocatalysts for the hydrogen evolution reaction(HER).However,their limited active sites and poor electric conductivity pose a significant hurdle to their HER perf
In a solution treated Co-20Ni-6Si shape memory alloy,coherent nano-particles were precipitated after annealing at 873 K for 1 min,but the shape memory effect al
Thin film capacitors with excellent energy storage performances,thermal stability and fatigue endurance are strongly desired in modern electrical and electronic