【摘 要】
：
Commercial spherical activated carbon (SAC) was modified by impregnation to enhance the catalytic properties of SAC in acetylene hydrochlorination through melamine modification. Different modification conditions for SAC with nitrogen were compared by chan
【机 构】
：
School of Chemistry and Chemical Engineering, Shihezi University/Key Laboratory for Green Processing
【出 处】
：
武汉理工大学学报（材料科学版）（英文版）
论文部分内容阅读
Commercial spherical activated carbon (SAC) was modified by impregnation to enhance the catalytic properties of SAC in acetylene hydrochlorination through melamine modification. Different modification conditions for SAC with nitrogen were compared by changing the SAC-Melamine ratios. The effect of carbonization temperature on the modification was also investigated. Surface chemistry and adsorption properties of the modified and unmodified SACs were studied by scanning electron microscope (SEM), X-ray photoelectron spectroscopy (XPS), elementary analysis, BET, and temperature-programmed desorption (TPD). Moreover, the catalytic properties of SAC in acetylene hydrochlorination under differently modified conditions were also investigated. Elemental analysis showed that the nitrogen content of the modified SAC was greatly improved. XPS revealed that nitrogen mainly exists in Pyrrole nitrogen and Pyridine nitrogen. TPD showed that desorption of C2H2 was changed by modification. The conversion rate of acetylene was up to 70%under the following reaction conditions:temperature, 150℃;C2H2 hourly space velocity (GHSV), 36 h-1;feed volume ratio V (HCl)/V (C2H2) = 1.15. The catalytic properties of SAC were improved significantly via melamine modification.
其他文献
In order to improve the wear resistance and restrain nickel release of TiNi alloys, the Mo modified layers on TiNi substrates were obtained using the double glow plasma surface alloying technique. Scanning electron microscopy (SEM), glow discharge optical
The Zn1-xCuxO polycrystalline materials were prepared by doping CuO into wurtzite ZnO through solid state reaction. The high concentration of copper doping in ZnO exhibited remarkable room temperature ferromagnetism. The Experiments showed that the magnet
The chloride ion transmission model considering diffusion and convection was established respectively for different zones in concrete by analyzing chloride ion transmission mechanism under the drying-wetting cycles. The finite difference method was adopte
We prepared graphene(GE) with a mean size of 3087 nm. The transition of graphene oxide (GO) to GE was conifrmed by UV-visible spectroscopy, Fourier transform infrared spectroscopy (FTIR) and X-ray diffraction (XRD). The experimental results of optical mic
Our researches are based on the fact that the systems composed of polyacrylamide and montmorillonite under a kind of shear state often appear in some important practical processes like drilling welletc. The viscosity of polyacrylamide is usually the most
The influence of Al content on microstructure characterization and indentation hardness testing behavior of Mg-8Sn-xAl(x=1 wt%, 2 wt%, 3 wt%)-1Zn alloys was investigated by optical microscope, Pandat software, X-ray diffraction, scanning electron microsco