The Micro-structural Studies ofNi-BaTiO3 Nanocomposite Films by TEM and EELS
【作 者】
:
【机 构】
:
Institute of Atomic and Molecular Physics, Sichuan University, Chengdu 610065, China;Research Center
【出 处】
:
武汉理工大学学报(材料科学版)(英文版)
【发表日期】
:
2011年5期
其他文献
Characterization and Luminescence Properties of a New Europium (Ⅲ) Complex with a Macrocyclic Ligand
A series of thermoreversible konjac glucomannan gels crosslinked by organic bo-rate were prepared.Required amount of hydrophilic SiO_2 was added into the konjac glucomannan solutions before the crosslinking reaction.The gel network was formed through the
The normal asphalt index test,DSR test,FTIR and the GPC distribution analysis of molecular weight on the extraction and recovery of asphalt of the gussasphalt,SMA extraction and recovery of asphalt and the rotary-thin-film-oven-aged asphalt above 240℃were
Prediction of Mechanical Properties of 50CrVA Tem-pered Steel Strip for Horn Diaphragm Based on BPAN
50CrVA cold-rolled spring steel strip was used to fabricate the diaphragm of the automotive horn.The material parameters which were taken into account in the design of the dia-phragm involve elongation,elastic limit,Young\'s modulus,yield strength and t
Particle reinforced Sn-Zn based composite solders were obtained by adding Cu powders to Sn-9Zn melts. The microstructure analysis reveals that in situ Cu_5Zn_8 particles are formed and distributed uniformly in the composite solders. The strength and plast
Red mud was activated to be a mineral admixture for Portland cement by means of heating at different elevated temperatures from 400 ℃ to 700 ℃. Results show that heating was ef-fective, among which thermal activation of red mud at 600 ℃ was most effective
Astabilizedsoilstructureformation model wasintroduced. In ordertoformcompact stabilized soil structure, cementitious hydrates were needed to wrap and bind the soil aggregates.Meanwhile, expansible hydrates were needed to squeeze and fill the pores, especi
Degradation of Pore Structure and Microstructures in Hardened Cement Paste Subjected to Flexural Loa
Hardened cement paste was subjected to the flexural loading and wet-dry cycles in sea water.The degradation of microstructures was obtained using scanning electron microscope(SEM),and the energy dispersive spectrum(EDS)analysis was carried to analyze the