摘要：在桥梁正常使用期间内，由于车辆的不断提速和超重车辆的行驶，以及外界各种客观因素的作用和影响，会导致桥梁的结构产生不同程度的病害、出现缺陷，严重的会影响桥梁正常使用。本文通过对道路桥梁结构的分析，尤其是结构上所存在的危害形式和成因的分析，从而提出加固问题的重要性和主要方法。
关键词：道路桥梁；结构病害；裂缝修补；加固增强
Abstract: in the bridge during normal use, as the vehicle's speed and overweight vehicles constantly running, and various objective factors outside the role and impact of, will lead to the structure of the bridge produces different degree of disease, appear defects, serious can affect bridge of normal use. Based on the analysis of road and bridge structure, especially on the structure of the existing harm form and the analysis of the causes, and then puts forward the importance of the problem of reinforcement and the main method.
Keywords: road and bridge; Structure diseases; Crack repair; Reinforcement enhance
中图分类号：K928.78文献标识码：A 文章编号：
一、地震对桥梁病害的影响
地震对桥梁的破坏主要是由于地表破坏和桥梁受震破坏引起的。其中地表破坏有地裂、滑坡、塌方、岸坡滑移和砂土液化等现象。地裂会造成桥梁跨度的缩短、伸长或墩台下沉。在陡峻山区或砂性土和软黏土河岸处，强烈地震引起的塌方、岸坡滑动以及山石滚落，可使桥梁遭到破坏。
在浅层的饱和或疏松砂土处，地震作用易引起砂土液化，致使桥梁突然下沉或不均匀下沉，甚至使桥梁倾倒。在坡边土岸或古河道处，地震则往往引起岸坡滑移、开裂和崩坍等现象，造成桥梁破坏。桥梁受震破坏是由于地震使桥梁产生水平和竖直振动，造成桥梁构件的损坏和破坏,甚至使桥梁倒坍。此外,有些桥梁虽然在强度上能够承受地震的振动力，但由于桥梁上部、下部结构联结不牢、整体性差，往往会造成桥梁上部和下部结构间产生过大的相对位移，从而导致桥梁破坏。
梁桥受震破坏主要表现为：①墩台开裂、倾斜、折断或下沉；②支座弯扭、断裂、倾倒或脱落；③桥梁上部结构和下部结构间相对位移；④落梁。
拱桥受震破坏主要表现为:①拱圈开裂；②墩台下沉；③多孔时墩身开裂、折断；④落拱。一般说来，桥梁震害在高烈度震区比低烈度震区重，岸坡滑移和地基失效处的桥梁震害比一般地基处严重。
二、桥梁裂缝修补技术
裂缝修补的目的在于恢复结构物的防水性和耐久性，主要技术有：
1．表面处理法，在微裂缝的表面涂抹填料及防水材料，以提高其防水性和耐久性。对于宽度发生变化的裂缝，要设法使用有伸缩性的材料。
2．注浆法，在裂缝中注入树脂或水泥类材料，以提高其防水性及耐久性。主要注浆材料是环氧树脂，多采用低压低速注入法。环氧树脂注入法与钢钉并用，可以增强裂缝部位的整体性，是一种防止裂缝继续发展的好办法。
3．充填法，这是一种适合于修补较宽裂缝的方法，具体做法是沿裂缝凿一条深槽，然后在槽内嵌补各种粘结材料，如水泥砂浆、环氧砂浆、膨胀水泥砂浆、环氧树脂硅、沥青及各种化学补强剂等。
4．表面喷涂法，喷浆修补是一种在经凿毛处理的裂缝表面，喷射一层密实而且粘度高的水泥砂浆保护层，来封闭裂缝的修补方法。喷浆前，需要把结构表面的剥离部分除去，再用水冲洗清洁，并在开始喷浆之前把基层湿润，然后再开始喷浆。
5．粘结钢板封闭法,当钢筋硂构件产生主拉应力裂缝时，可对裂缝先进行处理之后，再在裂縫处粘结钢板，并用膨胀螺栓对钢板加压。钢板粘结方向应和裂缝方向垂直。
三、桥梁加固增强技术
梁式桥上部结构加固增强技术主要有加大截面加固法、外部粘贴加固法、外部预应力加固法、改变结构体系加固法、增设纵梁加固法。
加大截面加固法采用增大构件的截面面积，根据荷载大小和净空条件不同，可分为以加大截面面积为主和加配钢筋为主两种加固方案。
外部粘贴加固法系用型钢、玻璃钢等材料通过环氧树脂等粘合剂粘贴在结构外部，以提高结构承载能力的一种方法。适用于构件尺寸受限制但又必须大幅度提高结构承载能力的场合，必须保证粘和剂的质量
外部预应力加固法指运用预应力原理，在增设的构件或原有构件上施加一定初始应力的一种加固方法。采用对受拉区施加预加压力，可以抵消部分自重应力，起到卸载、减小跨中挠度、减小裂缝宽度或闭合裂缝的作用。
改变结构体系加固法通过增设支撑或桥墩，把简支变为连续、在梁下增设如钢架等加劲梁或叠合梁，以减小梁内控制截面峰值弯矩，提高承载能力的一种加固方法。
增设纵梁加固法在桥梁墩、台基础稳定，并具有足够承载能力的情况下，可采用增设承载能力高和刚度大的新纵梁，这些新梁与旧梁连接在一起共同受力。由于应运中的车辆荷载在新增主梁后的桥梁结构中重新分布，使原梁中所受荷载得以减少，加固后的桥梁承载能力和刚度得以提高。
四、桥梁结构加固新技术——锚喷
随着施喷机具的发展以及速凝剂的采用，人们把喷射硂与锚杆、钢筋网等配合起来使用，促进了锚喷技术的完善。实践证明，锚喷技术完全可以应用于桥梁上部结构的加固增强。
喷射硅的性能喷射硅在工艺材料及结构等方面与普通现浇硅相比有许多优点。施工中需加入速凝剂，因而又具有快凝、早期强度高的特点；锚喷技术不用或只用侧向模板，其运输、浇注、捣固合并为一道工序、设备简单、占地面积小、施工机械化程度高、速度快、效率高、节省劳动力；可设计性强，即按照加固整治的实际需要可在拱腹下施喷形成各种结构类型；不中断交通。
五、旧桥梁加铺沥青层修复施工技术
旧桥梁路面沥青加铺层的施工与新建公路沥青路面的施工基本相同，施工中主要环节为
1、处理破碎板：将原路面严重破碎板、严重裂缝、板角断裂等破碎板块挖除，用早强混凝土或早强钢筋混凝土进行修补至与原路面齐平，原路涵洞盖板铺装层出现破碎的也应一并处理；
2、稳定原路面板：对卿泥、脱空的混凝土面板及轻微、中等裂缝的面板进行板底压浆处理，使混凝土面板处于稳定状态。对使用时间较长，原路面基层为石灰土等水稳定性不良结构的路段，为保险起见，可对全部原有的混凝土面板进行压浆处理；
3、提高原路面防水能力：对所有缩缝、纵缝、裂缝清缝后，用填缝料灌缝。然后在原混凝土路面上加铺土工布隔离层或加铺1.5～2.5cm沥青混和料隔离层，不做隔离层的应洒布粘层油，以减少路表水下渗并提高加铺层与原路面的结合能力；
4、加铺沥青层：在隔离层(粘层)上加铺沥青混凝土面层一般应分为二层，下面层较厚(一般4～8cm)，采用热稳定性较好的开级配粗粒式或中粒式沥青碎石或沥青混凝土，上面层较薄(一般厚2～9cm)，采用防水性能较好的密级配细粒式或中粒式沥青混凝土。原水泥混凝土路面横坡较小时，通过沥青面层调整路面横坡不小于1.596。桥面部分可仅加铺上面层，桥头两端50m内的下面层应进行调坡。
面层原材料技术要求、配合比设计、拌和、摊铺等与常规沥青类路面施工相同。只是碾压时，选择压实机具吨位应考虑沥青层的厚度，防止过振引起沥青混合料二次细粒化。
结束语
为了保证交通畅通顺利，就需要在桥梁出现病害的时候对桥梁进行加固、维修和改造。桥梁结构常规裂缝机理的产生相当复杂,单因素裂缝是很少的。一般说来,裂缝主要是由一种或几种因素引起的,其它因素只是起了裂缝主要是起了裂缝继续发展或加剧劣化的作用。
关键词：道路桥梁；结构病害；裂缝修补；加固增强
Abstract: in the bridge during normal use, as the vehicle's speed and overweight vehicles constantly running, and various objective factors outside the role and impact of, will lead to the structure of the bridge produces different degree of disease, appear defects, serious can affect bridge of normal use. Based on the analysis of road and bridge structure, especially on the structure of the existing harm form and the analysis of the causes, and then puts forward the importance of the problem of reinforcement and the main method.
Keywords: road and bridge; Structure diseases; Crack repair; Reinforcement enhance
中图分类号：K928.78文献标识码：A 文章编号：
一、地震对桥梁病害的影响
地震对桥梁的破坏主要是由于地表破坏和桥梁受震破坏引起的。其中地表破坏有地裂、滑坡、塌方、岸坡滑移和砂土液化等现象。地裂会造成桥梁跨度的缩短、伸长或墩台下沉。在陡峻山区或砂性土和软黏土河岸处，强烈地震引起的塌方、岸坡滑动以及山石滚落，可使桥梁遭到破坏。
在浅层的饱和或疏松砂土处，地震作用易引起砂土液化，致使桥梁突然下沉或不均匀下沉，甚至使桥梁倾倒。在坡边土岸或古河道处，地震则往往引起岸坡滑移、开裂和崩坍等现象，造成桥梁破坏。桥梁受震破坏是由于地震使桥梁产生水平和竖直振动，造成桥梁构件的损坏和破坏,甚至使桥梁倒坍。此外,有些桥梁虽然在强度上能够承受地震的振动力，但由于桥梁上部、下部结构联结不牢、整体性差，往往会造成桥梁上部和下部结构间产生过大的相对位移，从而导致桥梁破坏。
梁桥受震破坏主要表现为：①墩台开裂、倾斜、折断或下沉；②支座弯扭、断裂、倾倒或脱落；③桥梁上部结构和下部结构间相对位移；④落梁。
拱桥受震破坏主要表现为:①拱圈开裂；②墩台下沉；③多孔时墩身开裂、折断；④落拱。一般说来，桥梁震害在高烈度震区比低烈度震区重，岸坡滑移和地基失效处的桥梁震害比一般地基处严重。
二、桥梁裂缝修补技术
裂缝修补的目的在于恢复结构物的防水性和耐久性，主要技术有：
1．表面处理法，在微裂缝的表面涂抹填料及防水材料，以提高其防水性和耐久性。对于宽度发生变化的裂缝，要设法使用有伸缩性的材料。
2．注浆法，在裂缝中注入树脂或水泥类材料，以提高其防水性及耐久性。主要注浆材料是环氧树脂，多采用低压低速注入法。环氧树脂注入法与钢钉并用，可以增强裂缝部位的整体性，是一种防止裂缝继续发展的好办法。
3．充填法，这是一种适合于修补较宽裂缝的方法，具体做法是沿裂缝凿一条深槽，然后在槽内嵌补各种粘结材料，如水泥砂浆、环氧砂浆、膨胀水泥砂浆、环氧树脂硅、沥青及各种化学补强剂等。
4．表面喷涂法，喷浆修补是一种在经凿毛处理的裂缝表面，喷射一层密实而且粘度高的水泥砂浆保护层，来封闭裂缝的修补方法。喷浆前，需要把结构表面的剥离部分除去，再用水冲洗清洁，并在开始喷浆之前把基层湿润，然后再开始喷浆。
5．粘结钢板封闭法,当钢筋硂构件产生主拉应力裂缝时，可对裂缝先进行处理之后，再在裂縫处粘结钢板，并用膨胀螺栓对钢板加压。钢板粘结方向应和裂缝方向垂直。
三、桥梁加固增强技术
梁式桥上部结构加固增强技术主要有加大截面加固法、外部粘贴加固法、外部预应力加固法、改变结构体系加固法、增设纵梁加固法。
加大截面加固法采用增大构件的截面面积，根据荷载大小和净空条件不同，可分为以加大截面面积为主和加配钢筋为主两种加固方案。
外部粘贴加固法系用型钢、玻璃钢等材料通过环氧树脂等粘合剂粘贴在结构外部，以提高结构承载能力的一种方法。适用于构件尺寸受限制但又必须大幅度提高结构承载能力的场合，必须保证粘和剂的质量
外部预应力加固法指运用预应力原理，在增设的构件或原有构件上施加一定初始应力的一种加固方法。采用对受拉区施加预加压力，可以抵消部分自重应力，起到卸载、减小跨中挠度、减小裂缝宽度或闭合裂缝的作用。
改变结构体系加固法通过增设支撑或桥墩，把简支变为连续、在梁下增设如钢架等加劲梁或叠合梁，以减小梁内控制截面峰值弯矩，提高承载能力的一种加固方法。
增设纵梁加固法在桥梁墩、台基础稳定，并具有足够承载能力的情况下，可采用增设承载能力高和刚度大的新纵梁，这些新梁与旧梁连接在一起共同受力。由于应运中的车辆荷载在新增主梁后的桥梁结构中重新分布，使原梁中所受荷载得以减少，加固后的桥梁承载能力和刚度得以提高。
四、桥梁结构加固新技术——锚喷
随着施喷机具的发展以及速凝剂的采用，人们把喷射硂与锚杆、钢筋网等配合起来使用，促进了锚喷技术的完善。实践证明，锚喷技术完全可以应用于桥梁上部结构的加固增强。
喷射硅的性能喷射硅在工艺材料及结构等方面与普通现浇硅相比有许多优点。施工中需加入速凝剂，因而又具有快凝、早期强度高的特点；锚喷技术不用或只用侧向模板，其运输、浇注、捣固合并为一道工序、设备简单、占地面积小、施工机械化程度高、速度快、效率高、节省劳动力；可设计性强，即按照加固整治的实际需要可在拱腹下施喷形成各种结构类型；不中断交通。
五、旧桥梁加铺沥青层修复施工技术
旧桥梁路面沥青加铺层的施工与新建公路沥青路面的施工基本相同，施工中主要环节为
1、处理破碎板：将原路面严重破碎板、严重裂缝、板角断裂等破碎板块挖除，用早强混凝土或早强钢筋混凝土进行修补至与原路面齐平，原路涵洞盖板铺装层出现破碎的也应一并处理；
2、稳定原路面板：对卿泥、脱空的混凝土面板及轻微、中等裂缝的面板进行板底压浆处理，使混凝土面板处于稳定状态。对使用时间较长，原路面基层为石灰土等水稳定性不良结构的路段，为保险起见，可对全部原有的混凝土面板进行压浆处理；
3、提高原路面防水能力：对所有缩缝、纵缝、裂缝清缝后，用填缝料灌缝。然后在原混凝土路面上加铺土工布隔离层或加铺1.5～2.5cm沥青混和料隔离层，不做隔离层的应洒布粘层油，以减少路表水下渗并提高加铺层与原路面的结合能力；
4、加铺沥青层：在隔离层(粘层)上加铺沥青混凝土面层一般应分为二层，下面层较厚(一般4～8cm)，采用热稳定性较好的开级配粗粒式或中粒式沥青碎石或沥青混凝土，上面层较薄(一般厚2～9cm)，采用防水性能较好的密级配细粒式或中粒式沥青混凝土。原水泥混凝土路面横坡较小时，通过沥青面层调整路面横坡不小于1.596。桥面部分可仅加铺上面层，桥头两端50m内的下面层应进行调坡。
面层原材料技术要求、配合比设计、拌和、摊铺等与常规沥青类路面施工相同。只是碾压时，选择压实机具吨位应考虑沥青层的厚度，防止过振引起沥青混合料二次细粒化。
结束语
为了保证交通畅通顺利，就需要在桥梁出现病害的时候对桥梁进行加固、维修和改造。桥梁结构常规裂缝机理的产生相当复杂,单因素裂缝是很少的。一般说来,裂缝主要是由一种或几种因素引起的,其它因素只是起了裂缝主要是起了裂缝继续发展或加剧劣化的作用。