【摘 要】
：
Based on crystal plasticity theory and surface layer model, relation of flow stress to billet dimension and grain size was built,and rationality of derived rela
【机 构】
：
National Die and Mold CAD Engineering Research Center
论文部分内容阅读
Based on crystal plasticity theory and surface layer model, relation of flow stress to billet dimension and grain size was built,and rationality of derived relation was verified with tensile tests of different size billets. With derived expressions, relation of decreasing flow stress scale effect to billet dimension, grain size as well as billet shape was discussed and predicted. The results show that flow stress is proportional to billet size; with decrease of grain size, flow stress is less influenced by billet dimension. When both cross section area and grain size are same, flow stress decrease of rectangular section billet or sheet is larger than that of circular section billet.
其他文献
The aggregating behavior between bubbles and particles induced by high intensity conditioning (HIC) was studied using high speed CCD technique. Bubble size meas
The melting, evaporation and oxidation behaviors as well as the solidification phenomena of tungsten and molybdenum in induction plasma were studied. Scanning e
The microwave magnetic properties of the ball milled FeCo panicles were investigated as func tions of ball milling time ( t ) using microwave electromagnetic pa
Nb-15W-18Si-xHf (x = 0, 5, 10 and 15, mole fraction, %) alloys were prepared by arc melting and then homogenized at1 750 ℃ for 50 h. The microstructure and mec
A finite element analysis was carried out on the development of residual stresses during the cooling process from the fabrication temperature in the SiCp reinfo
Impermeability of tunnel structural material after exposure to high temperature determines residual service life and security. The present study explores imperm
Eu3+ doped SiO2 nano-crystalline glasses were prepared by sol-gel method. The broad peak of XRD pattern indicates an amorphous SiO2 matrix. The affection of ann
Long lasting phosphorescence (LLP) was observed in Eu2+, Ce3+ co-doped strontium borate glasses prepared under the reducing atmosphere due to the emission of bo
Phase formation in ternary system of complex Sc, Na and Li phosphates was studied at 950 ℃ and synthesis of new phases of definite composition was carried out.
Er3+/Yb3+-codoped oxyfluoride crystallite glass was prepared with melting technique. The compositions and the melting temperature and the annealing temperature