Ni-Cr System solar selective thin solid films were prepared by d.c. magnetron reactive sputtering under the atmosphere of O2 and N2. Ni-Cr alloy was chosen as target material and copper sheets as substrate. Using SEAL Spectrophotometer and Talystep to analyze the relations between the selective characteristic and the structure, the formation and the thickness of the thin films. The aim is to obtain good solar selective thin films with high absorptance and low emittance, which is applied to flat plate solar heat collectors.
Ni-Cr System solar selective thin solid films were prepared by dc magnetron reactive sputtering under the atmosphere of O2 and N2. Using SEAL Spectrophotometer and Talystep to analyze the relations between the selective characteristic and the structure, the formation and the thickness of the thin films. The aim is to obtain good solar selective thin films with high absorptance and low emittance, which is applied to flat plate solar heat collectors.