【摘 要】
：
采用金相显微镜(OM)、X-射线衍射仪(XRD)、差热扫描仪(DSC)等分析手段对Mg-15Ca-15Zn-6Cu合金相变储热材料的组织结构与热物性参数进行了分析。通过反复熔化-凝固热循环试验,
论文部分内容阅读
采用金相显微镜(OM)、X-射线衍射仪(XRD)、差热扫描仪(DSC)等分析手段对Mg-15Ca-15Zn-6Cu合金相变储热材料的组织结构与热物性参数进行了分析。通过反复熔化-凝固热循环试验,研究了该合金的热循环稳定性。结果表明,Mg-15Ca-15Zn-6Cu合金经历1 000次热循环后的相变温度和相变潜热分别为510.2℃和198.7J/g,与循环前的初始合金相比,相变温度提高了5.5%,相变潜热减小了5.56%,因此,表现出良好的热循环稳定性。
The microstructure and thermal properties of Mg-15Ca-15Zn-6Cu alloy phase-change thermal storage materials were analyzed by OM, XRD and DSC. analysis. The thermal cycling stability of the alloy was studied by repeated melting-solidification thermal cycling tests. The results show that the phase transition temperature and phase transition latent heat of Mg-15Ca-15Zn-6Cu alloy after 1000 thermal cycles are 510.2 ℃ and 198.7J / g, respectively. Compared with the initial alloy before cycling, the phase transition temperature increases 5.5%, the latent heat of phase transformation is reduced by 5.56%, therefore, it shows good thermal cycle stability.
其他文献
目的:建立HPLC法测定祛斑合剂中丹参成份原儿茶酸含量。方法:色谱柱为Hypersil C18柱(200 mm×4．6 mm,5μm)流动相为甲醇-2．5％冰醋酸溶液(2．7:97．3),流速1．0 ml·min-1,检测波长为2
目的 探讨中药治疗免疫性不孕的临床疗效.方法 218例免疫性不孕患者,以玉屏风散加味为主方,水煎服,每日1剂,4周为1疗程,观察疗效.结果服药1～2个疗程.显效:156例,占71.6%;有效:
在不同的T4和T6热处理条件下,对Mg-7Al-1Si-1Gd合金的组织和硬度进行了研究。结果表明,T4(400℃×12h)固溶处理后β-Mg17Al12相几乎全部溶入α-Mg基体中,但Al2Gd相和汉字状Mg
通过Al-40Cu过共晶合金在10μm/s的凝固速率下定向凝固,得到了4mm×120mm铸锭。采用光学显微镜、成分分析等手段研究了定向凝固铸锭不同部位的凝固组织、宏观偏析等。结果
目的:选择注射用阿莫西林钠克拉维酸钾的最佳无菌检查方法,保证检验结果的准确和可靠性。方法:采用《中国药典》2005年版二部附录无菌检查法项下薄膜过滤法。结果:确定了注射
锁骨骨折在临床较为多见,约占全身骨折的5.98%[1],其手术内固定的方法也较多,疗效不一,现将我院自1998年1月至2006年2月对86例锁骨移位骨折采用重建钢板及克氏针内固定治疗结
该文从挂篮荷载计算、施工流程、支座及临时固结施工、挂篮安装及试验、合拢段施工、模板制作安装、钢筋安装、混凝土的浇筑及养生、测量监控等方面人手,介绍了S226海滨大桥
〔上接２００２年第１期名录（二）〕叶菜类１０４小叶杨（杨叶菜、明杨、南京白杨）（PopulussimoniiCarr．）①生境：多生于海拔１２００m以下的河岸及溪塘边或栽于村旁、屋后，呈片状和散生分布。②食用部分：嫩叶。③
由天津市滨海新区人民政府主办,天津滨海高新区管委会和SEMI China承办,友达光电协办,为期两天的“中国光伏产业发展论坛——滨海机遇”于11月8日在天津赛象酒店开坛。中国可
采用铝热还原法制备了Al-Ti-B中间合金,并对其进行静置-电极吸附-超声处理的联合净化处理。通过X射线衍射分析仪(XRD)、扫描电镜(SEM)和透射电镜(TEM)等对不同条件下的Al-Ti-