摘要:在建筑业中,由于许多建筑工程中存在屋面渗漏的问题,给建筑方、施工人员和居民带来了很大的困扰。粗陋的屋面防水会因为容易穿透、破坏而腐蚀建筑物的主体,时间久了就会严重影响楼宇的正常使用及对居民的日常生活造成影响,严重的情况下甚至可能对居民的生命安全带来威胁。本文施工存在的问题、材料选择、施工方面分析了屋面渗漏的原因,并提出了做好屋面防水的措施。
关键词:建筑工程屋面防水施工技术
Abstract: In the construction industry, because of the existence of roofing leakage many engineering problems, to the construction side, the construction workers and residents has brought great trouble. The humble roof waterproof because of easy penetration, damage and corrosion of building body, a long time will seriously affect the normal use of the building and the daily life of the residents affected, severe cases may even pose a threat to the safety of the residents. In this paper, the problems in construction, material selection, construction, analyses the reasons of roof leakage, and puts forward some measures of roof waterproof.
Keywords: construction; roof waterproofing; construction technology;
中圖分类号: TU57 文献标识码:A文章编号:
前言:屋面工程是建筑工程的一个重要的分部,是指屋盖面层的施工内容,它包括了屋面的防水工程和屋面的保温隔热工程。其由结构层以上的屋面找平层、隔汽层、保温隔热层、防水层、保护层或使用面层等结构层次所组成。其施工质量的优劣将直接关系到建筑物的使用寿命。近年来,虽然各种新型防水材料相继问世,但由于价格较高,缺乏施工经验,且耐久性还有待于进一步检验等原因,目前还是采用较为常规的材料为主。采用刚性防水和柔性防水相结合的办法,理论上可提高屋面的防水,而在实际施工过程中,或多或少地存在一些不够重视底层刚性防水层的心理,使得刚性防水层开裂,起鼓或渗漏,这样刚性防水层形同虚设,加上柔性防水层也存在其 自身的缺点,因而“双重保险”也不能有效防止屋面渗漏。
1 屋面防水施工存在的问题
1.1设计单位不重视防水设计防水层的选材本该由设计人员严格按“规范”要求进行, 这本是设计单位的责任与义务。但因不少设计人员不熟悉防水材料的品质,随意套用施工图集。建设单位干预防水设计,设计人员放弃自己的职责,将防水材料选材由建设单位决定, 从而导致设计阶段失去对建筑防水工程的质量控制 。
1.2建筑防水材料质量不符合质量要求目前防水材料市场的基本状况仍处于鱼目混珠、良莠不齐、真假难辨、假冒伪劣产品屡禁不止的局面,且有进一步蔓延之势。特别是主导产品SBS 改性沥青防水卷材受到的冲击最大。伪劣产品以比合格产品60%以上的价格,且市场占有率很大,使原来生产合格产品的优秀企业难以生存 。
1.3施工单位质量控制意识不强,假冒伪劣防水材料泛滥, 紧跟着的是将防水工程造价压得很低,使正规的防水专业施工公司难以中标。相反,这些工程就落到了无资质去挂靠别人的低素质包工队手中,以转包、违法分包的形式承接防水工程。这些包工队拿得出齐全的“合格”证明,通过大力功“关”,可以屡屡中标,然后大肆偷工减料,雇用廉价农民粗放作业。一旦发生渗漏,则用几桶涂料修修补补就可对付两年,所获得利润仍可大于“损失”这种状况, 对提高施工质量要求的只是一句空话。
2 防水施工工艺及防水材料的类别
2.1屋面防水工程根据所采用的防水材料不同材性可分为刚性防水屋面和柔性防水屋面。刚性防水屋面是指采用浇筑防水混凝土、涂抹防水砂浆或铺设烧结平瓦、水泥平瓦进行防水的屋面;柔性防水屋面是指采用铺设防水卷材、油毡瓦、涂刷防水涂料等进行防水的屋面。屋面依据其防水层所采用的防水材料材质不同,则又可分为刚性混凝土防水屋面、平瓦屋面、卷材防水屋面、涂膜 防水屋面、油毡瓦防水屋面、金属板材防水屋面等。根据其防水的方法不同,还可分为复合防水和结构白防水。
2.2根据屋面防水等级要求合理选用相应的防水材料,防水等级为Ⅰ级,宜选用合成高分子防水卷材、高聚物改性沥青防水卷材、金属板材、合成高分子防水涂料、细石混凝土等材料;防水等级为Ⅱ级,宜选用高聚物改性沥青防水卷材、合成高分子防水卷材、金属板材、合成高分子防水 涂料、高聚物改性沥青防水涂料、细石混凝土、平瓦、油毡瓦等材料; 防水等级为Ⅲ级,宜选用三毡四油沥青防水卷材、高聚物改性沥青防水卷材、合成高分子防水卷材、金属板材、高聚物改性沥青防水涂料、合成高分子防水涂料、细石混凝土、平瓦、油毡瓦等材料;防水等级为 Ⅳ,选用材料可选用二毡三油沥青防水卷材、高聚物改性沥青防水涂料等材料。
3 屋面防水施工技术
3.1分格缝的设置及做法
分格缝应设置在屋面板的支承端, 屋面转折处、防水层与突出屋面的交接处, 并应与屋面板缝对齐,使防水层因温差的影响,砼干缩结构变形等因素造成的防水层裂缝,集中到分格缝处,以免板面开裂。分格缝的设置间距不宜过大,当大于 6m 时,应在中部设“ v ”形分格缝,分格缝深度宜贯穿整个防水层厚度。当分格缝兼作排气道时, 缝可适当加宽,并设排气孔出气,当屋面采用石油、沥青、油毡作防水层对, 分格缝处应加200mm~ 300mm 宽的油毡,用沥青胶单边点贴, 分格缝内嵌填满油膏。
3.2屋面找平层做法
屋面采用建筑找坡与结构找坡相结合的做法。先按 3 %的结构找坡后,再在结构层上用1:6 水泥炉渣或水泥膨胀砼石找坡, 再做25mm 厚1:2.5水泥砂浆找平层,建筑找坡时, 一定要找准泛水坡度,流水方向,将晟高点与泄水口之间用鱼线拉直、打点、打巴、泄水口处厚度不得低r30mm 。浇砌时,一定要用滚筒和尺方滚、压赶、使其 密实 。
3.3屋面隔离层的做法
在施工中因地制宜,取长补短,把面上的这一层二布三油卷材防水层做在找平层与刚性层之间, 既起了隔离层的作用,又不被日晒雨淋,既防止油膏老化,又起了防水作用。在做卷材防水层施工时,应注意好 以下几点:
(1)基层上涂刮基层处理荆, 要求薄而均匀,一般干燥后,当不粘手才能铺贴卷材。
(2)卷材防水层的铺贴一般应由层面最低标高处向上平行屋脊施工, 使卷材按水流方向搭接, 当屋面坡度大于 10%时, 卷材应垂直于屋脊方向铺贴。
(3)铺贴方法:剥开卷材脊面的隔离纸, 将卷材粘贴于基层表面,卷材长边搭接保持50mm, 短边搭接保持 70mm,卷材要求保持自然松弛状态,不要拉得过紧,卷材铺妥后,应立即用平面振动器全面压实,垂直部位用橡胶榔头敲实。
(4)卷材搭接粘结:卷材压实后,将搭接部位掀开,用油漆刷将搭接粘接剂均匀涂刷, 在掀开卷材接头之两个粘接面,涂后干燥片刻手感不粘时,即可进行粘合,再用橡胶榔头敲压密实,以免开缝造成漏水。
(5)防水层施工温度选择5 ℃以上为宜。
3.4钢筋网片及细石砼刚性防水层的做法
在混凝土防水层中, 应配双向5@ 200x200 的冷拔钢筋网片,并在分格缝处断开, 以增强防水层刚度和板块的整体性, 钢筋网片在防水层中的布置应在尽量偏上的部位, 因为防水层表面受温差变化影响大而易产生裂缝 同时考虑表面碳化对钢筋的影响,因此, 钢筋网片的保护层厚度不得小于10mm 。细石砼防水层的强度等级不应小于C25,且应采用机械搅拌,机械振捣,砼的水灰比不应大于0.55,水泥标号不应低于42.5R。砼的厚度不应小于40mm,如过薄,砼失水很快,水泥不能充分水化,从而降低砼的抗渗性能。防水层的表面处理要重视, 面板要求厚薄一致,排水坡度要符合规范要求, 砼收水后进行二次压光,以切断和封闭砼中的毛细管,提高抗渗性。抹压面层时,严禁在表面洒水,加水泥浆或撒干水泥,以防龟裂脱皮降低防水效果。
防水砼浇筑 l2小时~24小時,即可进行养护,覆盖时间不小于l4小时。养护初期不得上人,砼的养护是细石砼防水层的极其重要的最后一道工序。养护不好会造成砼早期脱水,不但降低砼的强度, 而且会由于干缩引起砼内部裂缝表面起砂,使抗渗性能大幅度降低。
3.5屋面泛水、滴水、管道周边等细部处理
屋面泛水、滴水、管道周边 以及其它节点严格按设计图纸和技术规范施工,泛水平整光滑, 滴水无缺棱掉角,管道周边做到嵌缝密实,表面密封处理,檐口顶梁和外侧面事先找平及粉刷面层, 做好水电管路、避雷带的预埋工作,严禁在混凝土板浇捣后随意凿打。对个别后置穿板管道周边,必须二次分层灌浆, 孔洞应凿成上大下小的喇叭口,光滑塑料管应先拉毛表面后安装,与混凝土的粘结力和密实性。确保屋面防水工程质量是一个系统工程。
结语:屋面防水的质量, 除了要控制好施工质量外, 防水材料的性能和质量、防水设计的科学与合理等都是影响其质量的重要因素,均应加以重视。总体上讲,防止屋面渗漏, 设计是前提,材料是基础, 施工是关键,维修管理是保证。只有严把材料关, 精心设计, 精心施工,才能保证屋匠的防水质量,才能保证住户住着舒心。
关键词:建筑工程屋面防水施工技术
Abstract: In the construction industry, because of the existence of roofing leakage many engineering problems, to the construction side, the construction workers and residents has brought great trouble. The humble roof waterproof because of easy penetration, damage and corrosion of building body, a long time will seriously affect the normal use of the building and the daily life of the residents affected, severe cases may even pose a threat to the safety of the residents. In this paper, the problems in construction, material selection, construction, analyses the reasons of roof leakage, and puts forward some measures of roof waterproof.
Keywords: construction; roof waterproofing; construction technology;
中圖分类号: TU57 文献标识码:A文章编号:
前言:屋面工程是建筑工程的一个重要的分部,是指屋盖面层的施工内容,它包括了屋面的防水工程和屋面的保温隔热工程。其由结构层以上的屋面找平层、隔汽层、保温隔热层、防水层、保护层或使用面层等结构层次所组成。其施工质量的优劣将直接关系到建筑物的使用寿命。近年来,虽然各种新型防水材料相继问世,但由于价格较高,缺乏施工经验,且耐久性还有待于进一步检验等原因,目前还是采用较为常规的材料为主。采用刚性防水和柔性防水相结合的办法,理论上可提高屋面的防水,而在实际施工过程中,或多或少地存在一些不够重视底层刚性防水层的心理,使得刚性防水层开裂,起鼓或渗漏,这样刚性防水层形同虚设,加上柔性防水层也存在其 自身的缺点,因而“双重保险”也不能有效防止屋面渗漏。
1 屋面防水施工存在的问题
1.1设计单位不重视防水设计防水层的选材本该由设计人员严格按“规范”要求进行, 这本是设计单位的责任与义务。但因不少设计人员不熟悉防水材料的品质,随意套用施工图集。建设单位干预防水设计,设计人员放弃自己的职责,将防水材料选材由建设单位决定, 从而导致设计阶段失去对建筑防水工程的质量控制 。
1.2建筑防水材料质量不符合质量要求目前防水材料市场的基本状况仍处于鱼目混珠、良莠不齐、真假难辨、假冒伪劣产品屡禁不止的局面,且有进一步蔓延之势。特别是主导产品SBS 改性沥青防水卷材受到的冲击最大。伪劣产品以比合格产品60%以上的价格,且市场占有率很大,使原来生产合格产品的优秀企业难以生存 。
1.3施工单位质量控制意识不强,假冒伪劣防水材料泛滥, 紧跟着的是将防水工程造价压得很低,使正规的防水专业施工公司难以中标。相反,这些工程就落到了无资质去挂靠别人的低素质包工队手中,以转包、违法分包的形式承接防水工程。这些包工队拿得出齐全的“合格”证明,通过大力功“关”,可以屡屡中标,然后大肆偷工减料,雇用廉价农民粗放作业。一旦发生渗漏,则用几桶涂料修修补补就可对付两年,所获得利润仍可大于“损失”这种状况, 对提高施工质量要求的只是一句空话。
2 防水施工工艺及防水材料的类别
2.1屋面防水工程根据所采用的防水材料不同材性可分为刚性防水屋面和柔性防水屋面。刚性防水屋面是指采用浇筑防水混凝土、涂抹防水砂浆或铺设烧结平瓦、水泥平瓦进行防水的屋面;柔性防水屋面是指采用铺设防水卷材、油毡瓦、涂刷防水涂料等进行防水的屋面。屋面依据其防水层所采用的防水材料材质不同,则又可分为刚性混凝土防水屋面、平瓦屋面、卷材防水屋面、涂膜 防水屋面、油毡瓦防水屋面、金属板材防水屋面等。根据其防水的方法不同,还可分为复合防水和结构白防水。
2.2根据屋面防水等级要求合理选用相应的防水材料,防水等级为Ⅰ级,宜选用合成高分子防水卷材、高聚物改性沥青防水卷材、金属板材、合成高分子防水涂料、细石混凝土等材料;防水等级为Ⅱ级,宜选用高聚物改性沥青防水卷材、合成高分子防水卷材、金属板材、合成高分子防水 涂料、高聚物改性沥青防水涂料、细石混凝土、平瓦、油毡瓦等材料; 防水等级为Ⅲ级,宜选用三毡四油沥青防水卷材、高聚物改性沥青防水卷材、合成高分子防水卷材、金属板材、高聚物改性沥青防水涂料、合成高分子防水涂料、细石混凝土、平瓦、油毡瓦等材料;防水等级为 Ⅳ,选用材料可选用二毡三油沥青防水卷材、高聚物改性沥青防水涂料等材料。
3 屋面防水施工技术
3.1分格缝的设置及做法
分格缝应设置在屋面板的支承端, 屋面转折处、防水层与突出屋面的交接处, 并应与屋面板缝对齐,使防水层因温差的影响,砼干缩结构变形等因素造成的防水层裂缝,集中到分格缝处,以免板面开裂。分格缝的设置间距不宜过大,当大于 6m 时,应在中部设“ v ”形分格缝,分格缝深度宜贯穿整个防水层厚度。当分格缝兼作排气道时, 缝可适当加宽,并设排气孔出气,当屋面采用石油、沥青、油毡作防水层对, 分格缝处应加200mm~ 300mm 宽的油毡,用沥青胶单边点贴, 分格缝内嵌填满油膏。
3.2屋面找平层做法
屋面采用建筑找坡与结构找坡相结合的做法。先按 3 %的结构找坡后,再在结构层上用1:6 水泥炉渣或水泥膨胀砼石找坡, 再做25mm 厚1:2.5水泥砂浆找平层,建筑找坡时, 一定要找准泛水坡度,流水方向,将晟高点与泄水口之间用鱼线拉直、打点、打巴、泄水口处厚度不得低r30mm 。浇砌时,一定要用滚筒和尺方滚、压赶、使其 密实 。
3.3屋面隔离层的做法
在施工中因地制宜,取长补短,把面上的这一层二布三油卷材防水层做在找平层与刚性层之间, 既起了隔离层的作用,又不被日晒雨淋,既防止油膏老化,又起了防水作用。在做卷材防水层施工时,应注意好 以下几点:
(1)基层上涂刮基层处理荆, 要求薄而均匀,一般干燥后,当不粘手才能铺贴卷材。
(2)卷材防水层的铺贴一般应由层面最低标高处向上平行屋脊施工, 使卷材按水流方向搭接, 当屋面坡度大于 10%时, 卷材应垂直于屋脊方向铺贴。
(3)铺贴方法:剥开卷材脊面的隔离纸, 将卷材粘贴于基层表面,卷材长边搭接保持50mm, 短边搭接保持 70mm,卷材要求保持自然松弛状态,不要拉得过紧,卷材铺妥后,应立即用平面振动器全面压实,垂直部位用橡胶榔头敲实。
(4)卷材搭接粘结:卷材压实后,将搭接部位掀开,用油漆刷将搭接粘接剂均匀涂刷, 在掀开卷材接头之两个粘接面,涂后干燥片刻手感不粘时,即可进行粘合,再用橡胶榔头敲压密实,以免开缝造成漏水。
(5)防水层施工温度选择5 ℃以上为宜。
3.4钢筋网片及细石砼刚性防水层的做法
在混凝土防水层中, 应配双向5@ 200x200 的冷拔钢筋网片,并在分格缝处断开, 以增强防水层刚度和板块的整体性, 钢筋网片在防水层中的布置应在尽量偏上的部位, 因为防水层表面受温差变化影响大而易产生裂缝 同时考虑表面碳化对钢筋的影响,因此, 钢筋网片的保护层厚度不得小于10mm 。细石砼防水层的强度等级不应小于C25,且应采用机械搅拌,机械振捣,砼的水灰比不应大于0.55,水泥标号不应低于42.5R。砼的厚度不应小于40mm,如过薄,砼失水很快,水泥不能充分水化,从而降低砼的抗渗性能。防水层的表面处理要重视, 面板要求厚薄一致,排水坡度要符合规范要求, 砼收水后进行二次压光,以切断和封闭砼中的毛细管,提高抗渗性。抹压面层时,严禁在表面洒水,加水泥浆或撒干水泥,以防龟裂脱皮降低防水效果。
防水砼浇筑 l2小时~24小時,即可进行养护,覆盖时间不小于l4小时。养护初期不得上人,砼的养护是细石砼防水层的极其重要的最后一道工序。养护不好会造成砼早期脱水,不但降低砼的强度, 而且会由于干缩引起砼内部裂缝表面起砂,使抗渗性能大幅度降低。
3.5屋面泛水、滴水、管道周边等细部处理
屋面泛水、滴水、管道周边 以及其它节点严格按设计图纸和技术规范施工,泛水平整光滑, 滴水无缺棱掉角,管道周边做到嵌缝密实,表面密封处理,檐口顶梁和外侧面事先找平及粉刷面层, 做好水电管路、避雷带的预埋工作,严禁在混凝土板浇捣后随意凿打。对个别后置穿板管道周边,必须二次分层灌浆, 孔洞应凿成上大下小的喇叭口,光滑塑料管应先拉毛表面后安装,与混凝土的粘结力和密实性。确保屋面防水工程质量是一个系统工程。
结语:屋面防水的质量, 除了要控制好施工质量外, 防水材料的性能和质量、防水设计的科学与合理等都是影响其质量的重要因素,均应加以重视。总体上讲,防止屋面渗漏, 设计是前提,材料是基础, 施工是关键,维修管理是保证。只有严把材料关, 精心设计, 精心施工,才能保证屋匠的防水质量,才能保证住户住着舒心。