【摘 要】
：
Dynamic crystallization was introduced to improve the magnetic properties of NdFeB nanocrystalline permanent magnets by optimizing microstructure. The microstru
【机 构】
：
Department of Material Science and Engineering
论文部分内容阅读
Dynamic crystallization was introduced to improve the magnetic properties of NdFeB nanocrystalline permanent magnets by optimizing microstructure. The microstructure was studied by X-ray diffraction (XRD) and transmission electron microscopy (TEM). It has been determined that, compared with the conventional heat treatment, dynamic crystallization can shorten the crystallization time. Moreover, dynamic crystallization can refine grains, enhance the exchange-coupled interaction among grains, and promote the magnetic properties. As a result, the optimal magnetic properties of Nd10.5(FeCoZr)83.4B6.1(Br＝0.685T, Hci ＝732 kA·m -1 , Hcb ＝429 kA·m-1 ,( BH )m=75 kJ·m -3 ) are obtained after dynamic crystallization heat treatment at 700 ℃ for 10 min.
其他文献
Based on a single ion model, Hamiltonian of the simplest form about magnetocrystalline anisotropy for Tb3+ ion was solved by using the numerical method. The rel
The differential equations for planar impacts reduce to an algebraic form, and can be easily solved. For three dimensional impacts with friction, there is no cl
生产调度问题是企业生产过程中的重要组成部分,合理、有效的调度方案尤其对提高间歇过程的生产效率和经济效益具有重要的意义.针对中间存储时间受限的间歇式调度问题,考虑了
The structure, Curie temperature and magnetostriction of Pr0.15Tb0.30Dy0.55Fe1.85Cx (x=0-0.1) compounds were investigated by X-ray diffraction, a vibrating samp
V2O5-WO3/TiO2 catalysts were prepared by impregnation method and in situ electrical conductivity measurements were carried out to investigate the reaction mecha
In order to obtain ultrafine Nd-Fe-B powder, a spray-dried precursor was treated by reduction-diffusion (R/D) process.And, unlike the conventional R/D process,
Thick GaN layer deposited by hydride vapor phase epitaxy (HVPE) on a metalorganic chemical vapor deposition (MOCVD) GaN template with a thin low temperature (LT
Aluminum-doped zinc oxide (AZO) thin films were deposited on sapphire (002) andglass substrates by two different sputtering techniques radio frequency magnetron
The professional modeling software package CrysVUn was employed to study the process of a large sapphire single crystal growth using Kyropoulos method.The influ
The rheological behavior of fumed silica suspensions in polyethylene glycol(PEG) was studied at steady and oscillatory shear stress using AR 2000 stress control