论文部分内容阅读
SmxCo5 (x=1.3, 0.7, 0.4) thin films were prepared by magnetron co-sputtering technique. The samples were annealed at 723 K under Ar atmosphere. The annealed time was chosen as 30 min. The hysteresis loops of the samples were measured under the ac applied