In this paper, a large-sized ingot of Mg?9Gd?3Y?1.5Zn?0.5Zr (wt%) alloy with a diameter of 600 mm was successfully prepared by the semi-continuous casting method. The alloy was subsequently annealed at a relatively low temperature of 430°C for 12 h a