The intermetallic compound Zr1-xHfxCo and Zr1-xScxCo(x=0,0.1,0.2,0.3) were prepared and their suitability for hydrogen storage was investigated. The alloys show single cubic phase identical with ZrCo by X-ray diffraction. Pressure-composition-temperature(