Mg-9Al-xRE magnesium alloys were studied, where x is 0, 0.4, 0.8, 1.2 and 1.6% (inweight percent, wt%), respectively. Influence of rare earths (RE) on microstru
The unstable dimensional distortion of LD31 aluminum alloy weldments at room temperature and after thermal cycles was studied by use of light interference and C
Mixed mode I//II fracture experiments of LC4-CS aluminum alloy were conducted by using tension-shear specimens with thicknesses of 2, 4, 8 and 14mm. Fracture me
The influence of the surface galvanic effects of 1Cr13 SS during cavitation damage hasbeen investigated in NaCl solutions. The results show that the solution co