Performance of RAP in the System of Cold Inplace Recycling of Asphalt Pavement
【机 构】
:
Key Laboratory for Silicate Materials Science and Engineering of Ministry of Education, Wuhan Univer
【出 处】
:
武汉理工大学学报(材料科学版)(英文版)
【发表日期】
:
2011年6期
其他文献
The process of preparing SiC coating by electron beam-physical vapor deposition (EB-PVD)was discussed from viewpoint of thermodynamis.Results show that within the temperature range of 2 700-3 300 K,the ratio of SiC in the SiC coating doesn\'t change muc
HfTiN film was deposited by co-reactive sputtering and then was annealed in dif-ferent gas ambients at temperature of 650 ℃ for 2 min to form HfTiON film. Capacitance-voltage and gate-leakage characteristics were investigated. The N2O-annealed sample exhi