Eu3+ -activated Gd2(MoO4)3 pseudo-pompon-like red-emitting phosphors were prepared by solid-state method.The structure,morphology,and luminescent properties of these powder samples were investigated by X-ray diffraction (XRD),scanning electron microscopy(SEM),and fluorescent spectrophotometry,respectively.The as-obtained phosphors were single crystalline phase with orthorhombic unit cell.The particles of the powder samples had the length of 5-12 μm and width of 3-7 μm with flake shape and large surface area,which is suitable for manufacture of white LEDs.The phosphor could be efficiently excited by the incident light of 348-425 nm,well matched with the output wavelength of near-UV (In,Ga)N chip,and re-emitted an intense red light peaking at 615 nm.By combing this phosphor with a～395 nmemitting (In,Ga)N chip,a red LED was fabricated,so that the applicability of this novel phosphor to white LEDs was confirmed.It is considered to be an efficient red-emitting conversion phosphor for solid-state lighting based on (In,Ga)N LEDs.