The 8%(mass fraction) yttrium-partially-stabilized zirconia(8YSZ) ceramic was fabricated via liquid phase sintering at 1 200-1 400 °C by adding different mass ratios of CuO-16.7%TiO2(molar fraction) as sintering aid.Relative density,microstructure,Vi