The changes of induced bone with four kinds of Ca-P ceramics after 2 years im-plantation in the dorsal muscles of rabbits were investigated.After 2 years implantation,mature bone (with a lamellar structure after the remodeling process)with bone marrow was
【机 构】
：
Oral Medicine Department of the Second Hospital,Hebei Medical University,Shijiazhuang 050000,China;D
【出 处】
：
武汉理工大学学报(材料科学版)(英文版)
论文部分内容阅读
The changes of induced bone with four kinds of Ca-P ceramics after 2 years im-plantation in the dorsal muscles of rabbits were investigated.After 2 years implantation,mature bone (with a lamellar structure after the remodeling process)with bone marrow was observed in HA1100 (HA,micro+macro porous),HA900(HA,micro+macro porous)and BCP(HA/TCP=7:3,mi-cro+macro porous),and no bone formation was observed in HA1200(HA,macro porous)ceramics. The induced bone neither disappeared nor grew uncontrollably,and was seen inside the pores of the implants or on the outer surface under the fibrous layer after 2 years.No bone formation was ob-served in the soft tissues distant from the implants.These results indicate that heterotopic bone for-mation induced by Ca-P materials did not give rise to uncontrolled growth over time,and the induced bone is limited to the inside or around the implants.Moreover,ectopic bone formation on the outer surface of the implants was detected in rabbits after 2 years.
其他文献
Rigid polyurethane foams were fabricated with five kinds of liquefied sugarcane bagasse polyols(LBP).The foams derived from sugarcane bagasse were investigated by thermogra-vimetric analysis(TGA),and the thermal degradation data were analyzed using the Co
Structure characteristics of three kinds of ceramsite with different water absorption and the influence on microstructure of interfacial zone as well as performance of chloride permeabil-ity and frost resistance of combined aggregate concrete were investi
Formation and coexistence of tricalcium silicate(C_3S)and calcium sulphoaluminate (C_4 A 3(S))minerals in Portland cement clinker containing calcium sulphoaluminate were investigated. The f-CaO content,mineral composite and formation of mineral in the cli
Spinel zinc ferrites ZnFe_2O)4,prepared by co-precipitation method using the zinc nitrate Zn(NO_3)_2·6H_2O and ferric nitrate Fe(NO_3)_3·2H_2O as the raw materials,were characterized by the thermo gravimetric analysis(TG)and differential scanning calorime
The effects of fly ash and MgO-type expansive agent on the shrinkage and expan-sive strain of concrete with high magnesia cement were investigated. The results show that high volumes of fly ash may reduce the shrinkage strain of concrete and inhibit the e