采用真空电子束焊对LY12铝合金进行焊接,分析了焊接速度、电子束流对焊缝组织的影响规律,并对接头拉伸性能进行了测试。试验结果表明,随着焊接速度增加或电子束流降低,焊缝组
【机 构】
：
南昌航空大学轻合金加工科学与技术国防重点学科实验室,
论文部分内容阅读
采用真空电子束焊对LY12铝合金进行焊接,分析了焊接速度、电子束流对焊缝组织的影响规律,并对接头拉伸性能进行了测试。试验结果表明,随着焊接速度增加或电子束流降低,焊缝组织逐步细化,接头强度增加,当电子束流为18 mA、焊接速度为1000 mm/min时,焊缝组织最细小,接头抗拉强度最高,为373.2 MPa。
The LY12 aluminum alloy was welded by vacuum electron beam welding, the influence of welding speed and electron beam current on the microstructure of the weld was analyzed, and the tensile property of the joint was tested. The experimental results show that as the welding speed increases or the electron beam current decreases, the microstructure of the weld gradually becomes thinner and the joint strength increases. When the beam current is 18 mA and the welding speed is 1000 mm / min, the microstructure of the weld is the smallest. The highest tensile strength was 373.2 MPa.
其他文献
釆用均匀设计法研究了药皮中大理石、萤石以及大理石和石英交互作用对FV520(B)不锈钢焊条的发红性、脱渣性以及飞溅性的影响。结果表明:随着焊条药皮中萤石含量的增加,FV520(
国家标准GB／T 223．63—1988采用分光光度法测定钢中锰的含量，是一种经典的分析方法，其测定结果的不确定度评定是实验报告的重要部分。通过对测定过程的重复性、标准曲线的制作、
在普朗克量子假说和爱因斯坦光量子假说基础上，提出了中基子(一种新的基本粒子)假说，揭示了光的量子性本质和原子光谱与原子结构及核外电子运动状态之间的关系。结果表明：光量子
2016年3月19日,由中国人民大学伦理学与道德建设研究中心、中国人民大学哲学院、中国人民大学出版社主办,中国伦理学会、《道德与文明》杂志社协办的罗国杰伦理思想研讨暨《
利用激光拉曼光谱内标法对异丙醇含量进行测定。研究了不同含量异丙醇与水特征峰相对强度比，建立了线性回归方程，结果表明：异丙醇线性范围为5％～40％，线性回归方程R=0．249 5w-0．304 7，相
对火焰原子吸收光谱法测定铜合金中镍含量的不确定度进行了评定，其不确定度来源于样品中镍的含量、样品溶解后的稀释体积及样品质量。通过对各不确定度分量的计算，最后计算出合
为观察皮下埋植避孕剂的远期效果，对129例接受埋植避孕剂的妇女进行了4年的随访。现将结果报道如下。1．对象：129例妇女于1992年12月～1994年6月皮下埋植长效避孕剂，埋植时年龄18－40
利用激光拉曼光谱法测定了硝酸异丙酯和四氯化碳，研究了不同体积比混合液的拉曼光谱，结果表明：硝酸异丙酯体积分数在1％～60％范围内与四氯化碳在459 cm-1处的特征峰强度呈线性关系，可
讨论了高氯酸钾重量法测定硝酸钾溶液中钾的不确定度的影响因素，给出了评定步骤。采用统计的方法得到了A类不确定度，利用所获得的各种信息对B类不确定度：包括样品质量、沉淀质量
提出了采用激光拉曼光谱法研究了硝酸乙酯及其在不同介质中的拉曼光谱。结果表明：以可乐和香油为溶剂时，当硝酸乙酯的体积分数达到60％时，可以被检测出。