Nd_ 8.1 Dy_ 0.9 Fe_ 76.95 Co_ 8.55 B_ 5.5 nanocomposite magnets annealed with and without a 10 T magnetic field were inv......

Ag/[BN/CoPt]5/Ag and [BN/Ag/CoPt]5/Ag thin films were deposited on glass substrates by magnetron sputtering and then ann......

利用逼近法和一些分析技巧，获得一类具强制位势常p-Laplace系统存在同宿解的一组充分条件．......

通过多靶射频磁控溅射系统在玻璃基片上制备了SmCo／Cu磁性薄膜．采用控制变量法优化了磁性层溅射工艺参数，制备出了矫顽力高达2400 Oe......

FeNi multilayer films were prepared by EB-PVD technique. A modified TG-DSCapparatus was used to measure their Curie temp......

用熔体快淬法制备了高性能纳米双相耦合Nd2Fe14B/α-Fe磁体, 研究了快淬速率和热处理工艺对其磁性能和微结构的影响. 实验结果表明......

制备了具有高矫顽力的2:17型SmCo磁体,采用透射电子显微镜对所制得的具有高矫顽力、低温度系数的2:17型磁体的微观组织进行了研究.......

制备了配以不同表面活性剂和基液的几种掺Ｚｎ的Ｆｅ３Ｏ４复合磁性液体。通过对其中磁性微粒颗粒度、分布均匀性的分析和复合磁性液体比饱和磁化......