Study of xonotlite architectural coatings for exterior wall insulation mechanism

来源 :2014中国功能材料科技与产业高层论坛 | 被引量 : 0次 | 上传用户：wwmmkk

【摘要】

：

Thermal insulation exterior wall coating has been successfully prepared, using styrene-acrylic emulsion as film former, and xonotlite as heat-insulating filler,which produced by hydrothermal reaction.

【作者】

：

L.Liu J.X.Cao

【出处】

：

2014中国功能材料科技与产业高层论坛

【发表日期】

：

2014年2期

【关键词】

：

xonotlite coatings thermal insulation walls mechanism

下载到本地 , 更方便阅读

下载此文赞助VIP

声明 : 本文档内容版权归属内容提供方 , 如果您对本文有版权争议 , 可与客服联系进行内容授权或下架

论文部分内容阅读

其他文献

碳纳米管的羧基化对环氧树脂复合材料拉伸强度及耐磨性的影响

环氧树脂由于固化后呈现出三维交联网络结构，呈现出质脆及耐磨性能较差的缺点，限制了其广泛应用。为了克服上述缺点，本文主要研究了羧基化碳纳米管的加入对环氧树脂复合材料拉伸强度和耐磨性的影响。

会议

碳纳米管环氧树脂羧基化拉伸强度耐磨性

Study on the Formaldehyde Adsorption Kinetics of Dry Waters

Dry waters with an average diameter of 82 μm were prepared by a high speed mixed route.The formaldehyde absorption kinetics of dry waters was investigated by simulating indoor formaldehyde pollution i

会议

Dry watersFormaldehydeAdsorption kinetics

Synthesis and Characterization of Poly (2-acrylamido-2-methyl propyl sulfonic acid-co-2-hydroxyethyl

A novel kind of AgNPs catalyst was synthesizedby in-situ reduction method using poly (2-acrylamido-2-methylpropylsulfonic acid-co-2-hydroxyethylmethclate)[shortas P(AMPS-co-HEMA)]hydrogel as matrices

会议

Silver nanoparticleCatalyst2-acrylamido-2-methylpropylsulfonic acid2-hydroxye

Graphene oxide/cement composites for electromagnetic interference shielding

Graphene oxide (GO) synthesized through a modified Hummers method was added into cement matrix to prepare GO/cement.Themicrostructure, mechanical properties, and the electromagnetic shielding effectiv

会议

graphene oxidecement-based compositeelectromagnetic interference shieldingmec

Multifunctionalities of Nanocarbon Materials Filled Cement-based Composites

Materials combined with a small amount of nanomaterials offer new possibilities in developing of multifunctional composites.Nanocarbon materials (NCMs) such as carbon nanotubes/ nanofibres, and nano g

会议

Nano carbon materialsCement-based compositesMechanical propertyDurabilityFun

DispersityonBarium-strontium Titanate Nanopowders by Microwave-hydrothermal Processing

Through the microwave-hydrothermal processing at 70℃ in 10 min, barium strontium titanate (BST) nanopowders are prepared by using butyl-titanate, barium nitrate and strontium nitrate as raw materials.

会议

barium strontium titanatedispersityOP-10polyethylene glycol 6000

Microstructure and properties of thermal sprayed ZrO2-NiCr coatings

NiCr/ZrO2 gradated coatings were obtainedon C45 carbon steel by high velocity arc spraying and micro-plasma spraying to improve the mechanical and thermalbehaviors of the carbon steel.

会议

Thermal SprayingMicrostructureHigh Temperature OxiditionThermal shock

Effect of the modification by Y, La and Chitosan for SO42-/ZrO2-TiO2-SiO2-Al2O3 type solid super aci

利用溶胶凝胶法制备SO24-/ZrO2-TiO2-SiO2Al2O3固体超强酸，并掺杂稀土元素钇、镧以及壳聚糖分别对其进行改性，利用其对丁酸己酯催化效能表征改性后的固体超强酸催化能力的变化。

会议

固体超强酸负载型催化剂掺杂改性

一种与软磁铁氧体成分共生的永磁铁氧体

本文介绍了一种与软磁铁氧体成分共生的永磁铁氧体的制作方法，通过能促进永磁铁氧体液相烧结的CaB2Si0.67O5.34添加剂的适量添加，获得了与组成式为CoFe2O4的软磁铁氧体成分共生的永磁铁氧体，磁体的显微结构、密度、磁性能均得到了显著的改善.

会议

共生软磁铁氧体永磁铁氧体

Study on the (Fe,Cr)7C3 particles reinforced ironbased composite coating

An iron based composite coating reinforced by (Fe,Cr)7C3 particles, with a thickness of 4.0 mm,was fabricated on the ductile castiron substrateby means of a centrifugal casting and in situ techniques.

会议

reinforcementIn situCompositecoating(FeCr)7C3

Study of xonotlite architectural coatings for exterior wall insulation mechanism

与本文相关的学术论文