【摘 要】
：
2-D layer structured Ti3C2 is synthesized using etching method under lower temperature,and then it is applied in dye-sensitized and perovskite solar cells as counter electrode with higher activity com
【机 构】
：
Inorganic Nano-materials of Hebei Province, College of Chemistry and Material Science,Key Laboratory
【出 处】
：
第八届新型太阳能材料科学与技术学术研讨会
论文部分内容阅读
2-D layer structured Ti3C2 is synthesized using etching method under lower temperature,and then it is applied in dye-sensitized and perovskite solar cells as counter electrode with higher activity compared with conventional TiC particles counter electrode.The dye-sensitized solar cells fabricated using 2-D layer structured Ti3C2 counter electrode achieves a power conversion efficiency of 9.57%,much higher than that of the counterpart device fabricated using TiC particles counter electrode (7.37%).The excellent activity of Ti3C2 electrode can be attributed to the superior charge transfer and mass transport properties owing to the specific 2-D layer structure.Moreover,the fabricated 2-D layer structured Ti3C2 is attempted to be applied in perovskite solar cells,thereby achieving a power conversion efficiency of 7.78% without further optimization.Thus,it exhibits a potential candidate to the noble metal electrodes.
其他文献
用两种不同的方法制备了球形及条形颗粒的Fe3O4磁流体，并用XRD、TEM、SEM分析测试手段对制备的样品进行了表征。将制备的两种形状的Fe3O4磁流体用于对制作的裂纹试块进行磁粉检测。试验结果表明：在磁化过程中，纯球形纳米Fe3O4向缺陷漏磁场处聚集较快，裂纹显示清晰具体；撤走外加磁场后，受磁悬液的扰动，缺陷磁痕被破坏；使用纯球形纳米Fe3O4磁悬液所得缺陷磁痕显示不如使用条形纳米Fe3O4磁悬
钙钛矿吸光层在各种老化条件下(尤其是在运行过程中)所体现出的不稳定性是制约其商业化应用的最大障碍。因此对器件运行过程中材料不稳定性来源的进一步了解对提升钙钛矿太阳能电池的运行稳定性有重要的指导意义。我们系统监测了FACs体系(FAxCS1-xPbI3)钙钛矿太阳能电池在不同老化条件下的性能衰退过程，发现在常温避光或85℃避光加热条件下器件展现出良好的稳定性，但在开压点以及最大功率点光照的运行条件下
2D/3D杂化钙钛矿薄膜的择优取向对于实现高效的太阳能电池至关重要.本工作中,我们在成膜过程中引入了一系列挥发性添加剂分子来制备C(CH3)3NH3+(TBA+)基2D/3D钙钛矿薄膜.基于原位紫外可见吸收光谱,原位PL测试,原位XRD测试和耗散石英晶体微天平(QCM-D)技术的表征,系统地研究了晶体生长过程和取向机制.我们发现挥发性添加剂能活化前驱体体系,且延长了PbI64-和阳离子之间的成核生
Rubidium cation (Rb+) doping has been witnessed to play a significant role in boosting comprehensive performances of organic-inorganic hybrid perovskite (OIHP) based photovoltaic devices.However,micro
The commonly employed formamidinium (FA)-containing perovskite solar cells (PSCs) exhibit severe phase instability problem,thereby limiting their commercial applications.Here,both phase stability and
Defects[1]and interface recombination loss[2]of the inverted perovskite solar cells (PSCs) are seriously impact on its performance and stability.Here,a kind of Symmetrical quaternary ammonium salt (SQ
全印刷介观钙钛矿太阳能电池因其低成本、高效率的特点备受学术界与产业界的广泛关注[1]。目前该构型器件报道的效率已超过17％[2,3]。钙钛矿前驱体在介孔结构中的自发扩散与结晶质量是影响该构型器件性能的两个重要因素。针对这些关键科学与技术问题,我们制备了由致密TiO2层、介孔TiO2层、介孔ZrO2层与碳电极构成的全印刷介观钙钛矿太阳能电池。系统研究了添加剂对钙钛矿薄膜结晶质量与器件性能的影响,采用
近年来,反式p-i-n结构钙钛矿太阳能电池(PSCs)由于其可忽略的迟滞、制备过程简单、及其与柔性和叠层器件的良好兼容性而受到越来越多的关注.其中,空穴传输材料(HTMs),负责空穴提取和传输,在反式PSCs中起着至关重要的作用.然而,常用的商用HTM材料,如聚[双(4-苯基)(2,4,6-三甲苯基)胺(PTAA),仍然存在成本高、聚合物的批次差异以及需要掺杂等问题.鉴于此,我们发明了一种新型吩噁
近年来,卤化铅钙钛矿由于其优良性能引起了广泛的关注,在温度、湿度和光照射下,通常单晶的性质比薄膜更加稳定[1].MAPbCl3具有较宽的禁带和较强的光吸收性能[2],MAPbCl3光电探测器具有优异的光电性能,目前,已有制作优良的MAPbCl3光电探测器,其响应度可达到3.73A W-1[3],它对光的吸收主要局限于波长小于420 nm的波段,光的禁带宽度约为2.9 eV[4].由于MAPbCl3
无机钙钛矿具有较好的湿热稳定性。本报告将首先汇报对无机钙钛矿CsPbIBr2薄膜进行调控的工作，在一步法制备的前驱体溶液中分别引入硫氰酸胍和醋酸甲脒这两种有机盐，发现它们可以增强(100)晶面取向，诱导形成大晶粒，改善薄膜的平整度，降低薄膜内部的缺陷。相应太阳电池的光电转换效率和稳定性得到明显提升。另外，针对CsPbIBr2薄膜与空穴传输层的界面，采用SrCl2处理的CsPbI3量子点进行缺陷钝化