【摘 要】
：
Lithium cobalt oxide (LiCoO2) with layered structure is the earliest found and widely employed cathode material for Li ion batteries (LIBs) due to its excellent cycling stability.Though its theoretica
论文部分内容阅读
Lithium cobalt oxide (LiCoO2) with layered structure is the earliest found and widely employed cathode material for Li ion batteries (LIBs) due to its excellent cycling stability.Though its theoretical capacity is around 274 mAh g-1,the practical capacity can only achieve to ～140 mAh g-1 when charged to 4.2 V (vs.Li/Li+),corresponding to de-intercalation of 0.5 Li per LiCoO2 [1].
其他文献
Nanostructured Fe3O4 is one of most commonly used active materials in the Li-ion battery,due to its high theoretical capacity (928mAhg-1)[1,2]and good electronic conductivity (2×104 Sm-1)[3].However,t
A new type of platelet-like ammonium vanadium bronze (NH4)2V6O16 is first used as cathode material for Na-ion battery.The discharge capacity and cycling stability is improved by the intercalation of t
A novel sulfur infiltration method via two-step of vacuum-vapor/melting adsorption was used to prepare high-rate performance sulfur-carbon composite cathodes.The hierarchical activated carbon (HAC) wi
The increasingly prominent energy and environment problems accelerate the rapid development of the lithium ion batteries.LiNi0.5Mn1.5O4 (LNMO) possessing a specific capacity of about 140 mA h g-1 and
In this paper,a very simple solution method is employed to coat amorphous MnO2 onto crystalline V2O5 nanoparticles grown on stainless steel substrate,which utilizes the better electrochemical performa
磷酸钒锂(Li3V2(PO4)3,LVP)是继磷酸铁锂之后的另一极具市场应用潜力的聚阴离子型正极材料.Li3V2(PO4)3具有斜方(NASCION)和单斜两种晶型.斜方晶系的电化学性能较差,不适合用作锂离子电池正极材料;而单斜结构Li3V2(PO4)3的热力学性质非常稳定,在锂离子电池中作为电极材料具有很大的潜力[1].
Graphene-sulfur (G-S) hybrid materials with sulfur nanocrystals anchored on interconnected fibrous graphene are obtained by a facile one pot strategy using a sulfur/carbon disulfide/alcohol mixed solu
橄榄石型结构的LiFePO4材料虽然具有环境友好、结构稳定的优点,但是其材料的电子电导率较低,约为10-9～10-10s·cm-1[1],锂离子在磷酸铁锂中的扩散系数为10-14-10-16m2·s-1[2].受制于极低的电子电导率和离子扩散系数,LiFePO4正极材料在高倍率条件下的性能较差,因此,提高LiFePO4正极材料的电导率和离子传输速率,改善LiFePO4正极材料的倍率性能是影响LiF
锂离子电池作为一种二次储能装置有很多的优点,且在商业化生产与实际应用中已占有重要地位.在商业生产中锂离子电池的主要研究方向是提高电池性能和降低电池成本,其中正极材料的成本接近整个锂离子电池成本的一半,且正极材料是限制锂离子电池比能量的关键因素.
Over the past decades,lithium-ion batteries (LIBs) have been widely utilized as optimal power sources for portable electronics,implantable medical devices and upcoming electrical vehicles.However,the