【摘 要】
：
Cellulose dissolved in 8% LiCl/dimethyl sulfoxide (LiCl/DMSO) via ethylenediamine (EDA) pretreatment was found to undergo reaction with tetraethyl orthosilicate (TEOS) at room temperature, forming tra
【机 构】
：
Jiangsu Provincial Key Lab of Biomass-based Green Fuel & Chemicals, College of Chemical Engineering,
论文部分内容阅读
Cellulose dissolved in 8% LiCl/dimethyl sulfoxide (LiCl/DMSO) via ethylenediamine (EDA) pretreatment was found to undergo reaction with tetraethyl orthosilicate (TEOS) at room temperature, forming transparent gels.This phenomenon apparently showed the TEOS undergo ester exchange with cellulose, and the multivalency of TEOS gave rise to crosslinking of dissolved cellulose.Several aspects of behavior of this system were consistent with this interpretation.The presence of trace EDA, arising from cellulose pretreatment, was essential for the reaction, probably acting as catalyst.Cellulose-silicate composite aerogels were prepared from these transparent gels after solvent exchange with ethanol followed by tert-butanol and freeze-drying.The aerogels were investigated by SEM, EDX and BET analysis (nitrogen gas adsorption).
其他文献
本文利用MQMC 2010(门窗)软件对塑料门窗影响塑料门窗热性能要素进行了模拟计算,通过软件模拟分析得出一些影响塑料门窗热性能的参数和结论，通过增加中空双侧玻璃的整体厚度、增加单片玻璃的厚度以及使用惰性气体的情况下，改变单一因素对玻璃整体传热系数改善较小；而通过增加气体层数目及使用Low-e玻璃的情况下，玻璃传热系数改善明显，可以作为主要考虑因素。
本发明是为了解决推拉门窗用胶条的密封性和滑动性功能兼顾的问题.该胶条由三种以上的TPV共挤出,通过各功能的拆分组合实现了取代目前使用的绒毛条,具有密封,隔音,无污染,便于清洗的特点.
基于ansys有限元分析,对挤出模具定型模设计中的水路排布方式,局部水孔形式,定型模配置多少及反应变量的取值等与否提出理论和数值依据,通过比较得出定型模的设计方案.
塑料异型材挤出模具行业的技术发展已趋向于成熟阶段,随着型材制造厂家对经济、高效、节能、环保的要求越来越高,这就要求高效地发挥挤出设备的生产效率,节约生产线的各项成本的投入.有效地提高塑料异型材挤出模具的挤出速度在其过程中起到了关键性的作用，经过多次的理论核算和实际试验,在提高模具的挤出速度方面取得了一定的成效.下面针对高速塑料异型材挤出模具的设计特点进行了总结，指出高速模具定型部分的设计，要充分的
Polyamide aerogels are synthesized with melamine and isophthaloyl chloride as starting materials, dimethylacetamide (DMAC) as acid-binding agent via sol-gel technology followed by carbon dioxide super
碳气凝胶作为一种新型纳米多孔材料,具有高比表面积、高中孔含量、高导电率、稳定的物理化学性能等优点,是制备双电层电容器电极的理想材料.本文以间苯二酚和甲醛为原料,碳酸钠为催化剂,通过溶胶-凝胶法和超临界干燥技术制备出具有三维多孔结构的碳气凝胶,并对其进行硝酸活化.通过循环伏安法、恒流充放电及循环性测试等考察材料的电化学性能.结果表明:在5mAm2电流密度和1.0V充放电电位条件下,经硝酸活化后,碳气
气凝胶是一种新型轻质、多孔纳米材料,其极高的孔隙率有效降低了材料的固相热导率,其纳米级孔结构可显著降低气体分子热传导和对流传热,因此气凝胶具有极低的热导率,是一种性能优异的高效隔热材料,广泛应用于航空、建筑、民用等领域.重点介绍了课题组氧化物气凝胶、碳气凝胶、多元气凝胶的制备方法.
采用溶胶-凝胶法和乙醇超临界干燥工艺,并经过高温热处理制备出自生长纳米锆纤维、纳米铝纤维增强SiO2复合气凝胶,通过SEM、TEM、XRD、BET等测试方法对复合气凝胶的机构进行了表征,并对试样的机械性能进行了初步验证.实验结果表明,利用前驱溶液中酸碱不平衡的现象自生长出锆、铝氧纳米纤维的思路,将金属氧化物和SiO2前躯体在凝胶老化过程中复合成型后再经高温转化的方式来实现增强纤维与气凝胶本体的完美
采用溶胶-凝胶法和乙醇超临界干燥工艺,以廉价的无机铝盐为原料,制备了完整块状的SiO2-Al2O3复合气凝胶.通过傅里叶红外光谱仪(FT-IR)和X射线衍射技术(XRD)来研究气凝胶在热处理过程中物相结构的变化;采用扫描电子显微镜(SEM)和透射电子显微镜(TEM)对气凝胶的表面形貌和组织结构进行观察;采用N2吸附-脱附实验来研究热处理过程中气凝胶孔结构的变化.结果表明,SiO2-Al2O3复合气
本文分析了游梁抽油机的负载特性,简要介绍了开关磁阻电机的工作原理及其应用于抽油机电机控制技术的特点和优势,并分析探讨了开关磁阻电机的控制结构及应用于抽油机系统的控制策略.并基于模拟抽油机负荷特性建立的开关磁阻电机实验平台进行了测试,结果表明开关磁阻电机应用于抽油机有很高的运行效率和节能效果.开关磁阻电机本身具有结构简单、可靠性高,控制灵活、调速性能好,运行效率高、温升低等优点,就其应用于抽油机系统