Study on NH4Cl under deposit corrosion behavior of carbon steel

来源 :国际腐蚀工程大会(ICEC2016) | 被引量 : 0次 | 上传用户：hnzxjl

【摘要】

：

【作者】

：

Guofu Ou Zhijian Zheng Kuanxin Wang Haozhe Jin Chao Wang

【机构】

：

The Flow Induced Corrosion Institution,Zhejiang Sci-Tech University,Hangzhou,Zhejiang 310018,China

【出处】

：

国际腐蚀工程大会(ICEC2016)

【发表日期】

：

2016年10期

下载到本地 , 更方便阅读

下载此文赞助VIP

声明 : 本文档内容版权归属内容提供方 , 如果您对本文有版权争议 , 可与客服联系进行内容授权或下架

论文部分内容阅读

　　The corrosion behavior and mechanism of under deposit corrosion of ammonium chloride salt of 10# carbon steel under various temperatures and relative humidity were investigated by the weight loss method.The corrosion behavior of the steel is closely related to the environment medium formed due to the salt deliquescence under various temperatures and relative humidity(RH).

其他文献

Revealing Blister Formation Process on Aluminum Surface in Hydrogen Environment

The corrosion resistance of metals relies on a passivating surface layer of dense and adherent oxide.However,the integrity of such a protective oxide is compromised in the presence of excess hydrogen

会议

Corrosion of The stainless clad steel with AC interference in concrete

The research of different gradient AC interference on corrosion rule of The 304 stainless clad steel was studied by polarization curve experiment in concrete.Results indicate that alternating current

会议

Electrodeposting Al-Mn coating on mild steel screws and its corrosion behavior

In this paper we show that screws made of mild steel can,in principle,be electrochemically coated with up to 20-μm-thick amorphous Al-Mn coatings in an ionic liquid composed of MnCl2-AlCl3-1-ethyl-3-m

会议

Materials Science Journals in IMR

Six science journals are published in the Institute of Metal Reasarch,Chinese Academy of Sciences(IMRCAS).In this reports,we introduce the history and current development of these journals in IMR,putt

会议

An Engineering Case According to the Application of Sea Sand in Reinforced Concrete

1.Engineering application environment: Sanshan island which located in the South Bank of Bohai Bay(Shandong),is a small peninsula surrounded by water on three sides.

会议

Sulfate-reducing bacteria induced the localized corrosion of Q235 steel

Localized corrosion behavior of Q235 steel in seawater containing sulphate-reducing bacteria(SRB)is investigated by wire beam electrode(WBE)technique,electrochemical measurement method and surface ana

会议

SRB induced accelerated corrosion attack of high strength steel under-0.85 VSCE cathodic polarizatio

Certain species of sulfate-reducing bacteria(SRB)use cathodes as electron donors for metabolism,and this electron transfer process may influence the proper protection potential choice for structures.

会议

The Novel Environment-friendly Chemical Conversion Nano Film

Surface and interfacial chemistry plays a critical role in developing advanced anti-corrosion systems,and the key to the successful coating system is the initial formation of a chemical conversion fil

会议

Failure analysis of pitted copper pipes used in underground water and preventive measures

The microbiologically influenced corrosion was investigated in the early failed copper pipes by pitting used in underground water.The bacteria were cultured by sampling from corrosion product near pit

会议

Erosion-corrosion of stainless steel at different locations of a 90-degree elbow

In this work,the passivation behavior and galvanic corrosion of 304 stainless steel elbow under erosion-corrosion(E-C)condition were studied by array electrodes technique through a loop system.

会议

Study on NH4Cl under deposit corrosion behavior of carbon steel

与本文相关的学术论文