【摘 要】
:
Alumina crusting behaviours were reviewed and were found to be closely related with α-Al2O3 content and LOI,particle size,bath ratio and temperature.Furthermore the cover properties such as density,ha
【机 构】
:
Zhengzhou Research Institute of CHALCO,Shangjie,Zhengzhou,P.R.CHINA 450041
【出 处】
:
2004年有色金属冶金及材料第二届国际学术会议
论文部分内容阅读
Alumina crusting behaviours were reviewed and were found to be closely related with α-Al2O3 content and LOI,particle size,bath ratio and temperature.Furthermore the cover properties such as density,hardness and strength,and thermal conductivity were discussed.
其他文献
Studies on the softening behavior of the 7005 alloy by means of real welding experiments and heat-affected zone (HAZ) simulation have been conducted. Softening in the HAZ is found to occur above a pea
本文简单介绍了我国的镁工业现状,概述了当前形式下轻量化技术的紧迫和镁合金所起的作用以及超强镁合金在航空航天等高端领域的应用,对超强镁合金制造工艺中非晶合金制备、快速凝固工艺以及变形加工方法,进行了理论分析和工艺的探讨,突出了非晶形成能力、晶化过程理论以及非晶粉末固结等关键工艺,为实际工作的开展形成必要的理论基础.
研究了采用高岭土型煤矸石为原料,经碳热还原制取的铝硅铁合金为还原剂热还原炼镁的工艺条件。发现,与传统的硅铁还原剂相比,此还原剂具有还原温度低、还原速度快、过量系数小、制团压力低等优点。经初步估算采用此种还原剂,在相同的还原率下,把每日二个生产周期改成每日三个生产周期是完全可能的。若如此,在镁的产量可增加产品产量约1/3的同时,镁的成本约降低1680元/吨镁左右。
Theoretical analysis and experiments,the different conductivity between impurities containing iron and silicon,and molten aluminum had been used to separate them from molten aluminum by electromagneti
本文研究氮化硅结合碳化硅耐火砖的抗腐蚀性和抗氧化性的测试方法,一种新的测试方法是在电解质中通入二氧化碳气体来模拟实际电解过程中电解槽内部的工作状态,这种新的测试方法测定了试样在电解质和二氧化碳共侵蚀作用下的性能,有利于了解电解槽内衬材料在铝工业电解中的腐蚀状况.且根据该方法制定了一个性能测试标准.同时测试了试样在高温下耐电解质、铝液的腐蚀性和在空气中的抗氧化性.这些测试方法简单易操作,且对于试样的
This paper reports a brief review of low-temperature electrolytes in aluminum electrolysis,the dissolution of alumina and aluminum in molten cryolite bath at 850-900℃.From these experiments it reveals
Nanoceramet were prepared by the heterogeneous precipitation,compact forming process of uniaxial die,and then airpressure sintering.These nanoceramet is used as the inert anodes of aluminium electroly
The work concerns on short term(4 hour)aluminum electrolysis tests of ZnFe2O4-based anodes.This was done as a screening test to evaluate the relative performance of the difference matedals.The results
NiAl2O4-metal composite material is an effective candidate for anodes used in industrial production of aluminium as a substitute for graphite anodes.NiAl2O4-Cu-Ni anode was prepared by Spark Plasma Si
本文研究了高炉铝酸钙炉渣的浸出动力学,考察了搅拌强度、浸出反应温度、浸出剂初始浓度以及炉渣粒度对浸出速率的影响。结果表明,浸出过程符合一级反应的收缩未反应核模型,宏观动力学方程为1+2(1-xB)-3(1-xB)2/3=[1.108exp(-1906/T)]t,其表观活化能为15.84KJ/mol。过程速率为固膜内扩散速率控制。通过用实验数据进行验证,表明所得模型能较好地描述炉渣的浸出过程。