【摘 要】
：
A series of the electrode materials (LiCoO2) for Lithium ion batteries were synthesized by radiating the mixture of Lithium oxide and Cobalt oxide in microwave field. The synthesizing conditions inclu
【机 构】
：
School of Materials and Metallurgy,Northeastern University,Shenyang 110004,China
【出 处】
：
2004年有色金属冶金及材料第二届国际学术会议
论文部分内容阅读
A series of the electrode materials (LiCoO2) for Lithium ion batteries were synthesized by radiating the mixture of Lithium oxide and Cobalt oxide in microwave field. The synthesizing conditions including reaction time, output power and reaction temperature were examned. And in the mean time, the structure and properties of LiCoO2 was characterized by using XRD, SEM technology and electrochemical testing method. The results showed that the output power and reaction time had a significant effect on the structure of products and that, the ordering layered structure of LiCoO2 had been obtained. In the tests of charge-discharge, it was found that the discharge capability of the first cycle was as high as 140mAhg-1. In comparison with conventional synthetic method, the microwave method can be energysaving, efficient with specious and clean working environment.
其他文献
为寻求降低湿法炼锌溶液净化过程中锌粉消耗的有效途径,本文研究了砷净液除钻工艺中返渣的利用、铜离子的加入量和净化pH值等因素对净化效果的影响.实验结果表明,净液过程中将第二、三段净液渣返回第一段净液的返渣技术能大幅度降低锌粉消耗,在净液温度70℃,搅拌速度200r/min,加入碱溶砒霜100mg/L,Cu2+的加入量为20mg/L,除钴pH为4.5的条件下除钴后液残钻浓度低于0.75mg/L,可使一
在热力学分析的基础上,进行了硅热还原法回收二次资源高速钢铁鳞中的W、Mo、Cr及V合金的研究.对还原剂、石灰用量及单位热效应对合金回收率的影响进行了分析探讨.研究结果表明：采用硅热法回收工艺是可行的,W、Mo回收率在95％以上,Cr回收率大于72％,V回收率不低于45％.冶炼出的产品质量稳定,可满足炼钢使用要求.充分做到了废物利用,具有明显的经济效益和社会效益.
本文模拟铜电解精炼的工业生产条件,研究高电流密度脉冲电流法电解精炼铜的方法,并用XRD、SEM研究脉冲电流对阴极铜沉积的结构和组成的影响。研究表明,当电解温度为70℃时,脉冲电解较适宜的工艺条件为：峰电流密度600 A/m2,脉冲宽度0.01 s,占空比1：1.添加剂用量：聚丙烯酰胺2.0 mg/dm3,硫脲1.5 mg/dm3,骨胶1.0 mg/dm3.测试结果表明,采用直流电解法得到铜沉积的晶
镁合金化学镀层的孔隙率与其耐蚀性有着直接的关系.根据基体元素与相应的指示剂显色原理,采用贴试纸法,对镁合金化学镀层的孔隙率测定进行了研究,并考察了镀液参数对孔隙率的影响.通过电子扫描电镜(SEM)和镀层的耐蚀性测试,验证贴试纸法测镁合金化学镀层孔隙率可行性.结果表明,铬黑T作指示剂溶液测定镁合金化学镀层孔隙率效果最佳,镁试剂I效果次之,茜素磺酸钠指示剂最差;采用贴试纸法测定化学镀层孔隙率是可行的;
A clear zinc hydrometallurgical process-the hydrometallurgy of zinc without iron residue was proposed in this paper. By using iron and part of zinc in the zinc sulfidc concentrates and manganese in py
Nickel-sulfur electrode was obtained in a modified Watts bath by adding thiourea (TU) into the bath. The effects of TU concentration, current density, temperature and pH value of electrodepositing sol
A new type of metal matrix composite with a composition of Al2O3-33.8Fe-26.2Ni (wt.％) used as inert anode was developed in this article. Aluminum electrolysis with this anode was conducted for 12 hour
The power feeding curve of graphitized furnace is a key technique in production of the electrode. The furnace is improved in order to reduce the power consumption of the electrode, to cut short the po
In the blast furnace slag, titanium disseminates in various mineral phases(perovskite, spinel, Ti-rich diopside, Ti(C、 N) and titannaugite). Based on the technique of selective precipitation, titanium
According to the thermogravimetric analysis of cobalt oxalate, different micropowder of Co3O4 was prepared from cobalt oxalate by thermal decomposition at different condition, which was characterized