【摘 要】
：
Lean duplex stainless steel,in which nickel is replaced by manganese and nitrogen,is one of the most important trends for developing high strength stainless steels.However,manufacturing thin gage stri
【机 构】
：
The State Key Laboratory of Rolling and Automation,Northeastern University,Shenyang Liaoning,China
【出 处】
：
第十届中国钢铁年会暨第六届宝钢学术年会
论文部分内容阅读
Lean duplex stainless steel,in which nickel is replaced by manganese and nitrogen,is one of the most important trends for developing high strength stainless steels.However,manufacturing thin gage strips of lean duplex stainless steelhas been one of the most challenging technologies in the production of stainless steels.In the present work,lean duplex stainless steel with the composition of Fe-18.7Cr-6.3Mn-0.38N was fabricated by twin-roll strip casting,in which serious pore defects can be effectively avoided as compared to conventional ingot casting.The solidification structure observed by OMindicates that no solidified dendrites have beenformedthrough surface to center of the cast strip,and the coarse equi-axedgrainswere formed in the center.The cast strip was hot rolled and cold rolled to the final thickness of 0.5mm,with no obvious edge cracks having been formed during both hot and cold rolling.After the annealing treatment at 1050°C for 5min following the cold rolling,distribution of Mn and Cr in the cast strip can be further homogenized.The cold rolled and annealed cast strip exhibited an excellent combinationof strength and ductility,with the ultimate tensile strength and elongation having been measured to be 1000MPa and 65%,respectively.TEM micrographs clearly showed that strain induced martensitic transformation had occurred during plastic deformation.
其他文献
水电与风电、光电协同运行是缓解新能源的电量效益和发电波动冲击之间的矛盾、克服新能源发展瓶颈的有效措施.鉴于现有的研究对发电波动刻画较为简单、对电力系统的架构和送出受阻时的弃电处理等考虑不足,影响了水风光电协同机制研究,本文构建了多目标、多层次、水风光电协同运行优化模型,以并网电量最大化和出力波动最小化为优化目标,考虑了电网的层级拓扑关系及弃电均衡处理.通过实例仿真,从并网电量、受阻电量和出力波动等
研究了模拟焊后热处理对14Cr1MoR钢组织和力学性能的影响。结果表明:采用正火(加速冷却)+回火生产的试验钢,显微组织以贝氏体为主,贝氏体板条的宽度范围为100～200nm,板条边界及板条内均分布有析出物颗粒,析出物颗粒的尺寸范围为50～100nm,而经过模拟焊后热处理的试验钢得到贝氏体和多边形铁素体的混合组织,贝氏体板条宽度增加,板条宽度范围为500～600nm;组织中的析出物明显长大,析出物
M701F4重型燃机余热锅炉的酸洗采用了浙江电科院独有的国内先进的DH-99A复合酸常温化学清洗工艺,首先用除盐水把余热锅炉系统的机械杂质冲洗掉,再用DH-99A复合酸对锅炉系统进行常温化学清洗,即清洗和钝化一次完成.经过化学清洗的金属表面清洁,无残留物,无点蚀,无二次锈,无过洗现象,无镀铜,形成完整的钝化膜.腐蚀指示片平均腐蚀速率小于8g/(m2·h),腐蚀总量小于80g/m2;除垢率大于90％
本文根据相似原理,采用物理模拟方法研究了在线钢包吹氩时渣-钢界面卷混行为及夹杂物的去除行为.研究了吹气量、渣层厚度和透气砖堵塞对渣-钢卷混的影响及在线底吹氩对夹杂物去除的影响.研究结果表明:在相同工艺条件下,随底吹气量增加钢液面裸露面积增加;随着钢包内钢液量减小吹开裸露面积逐渐减小.在恒定吹气量时,裸露面积比随着渣层厚度的增加而逐渐减小.在吹气量较小时,堵塞50％透气砖,顶部裸露面积和无堵塞相近;
Automatic quality monitoring for steel plate is a typical challenge in industries.Although there have been several research results at home and abroad,the requirements of defect detection and recognit
根据迁安2号高炉的实际生产条件和基础数据,通过计算煤粉在风口回旋区的不完全燃烧放热、煤粉的分解吸热、煤粉的成渣耗热以及煤粉带入硫分的脱硫耗热,计算出单位质量的煤粉的有效热量,通过高炉鼓风参数和炉顶的煤气成分计算高炉内碳的燃烧率,得出以下结论:煤粉能够用于高炉的有效热为5613.14～5614.49kJ/kg,碳在风口前的燃烧率为53.04％。
U75V钢轨在轧制过程中轨底出现裂纹,本文通过宏观观察,金相检验等方法对裂纹产生的原因进行分析,检验结果显示在轨底裂纹部位未观察到明显冶金缺陷,缺陷部位表层组织为回火索氏体+少量铁素体,与正常部位表层组织珠光体+铁素体不同.从上述分析结果可知轨底表面有淬硬层存在,淬火层组织已自回火,缺陷的产生与该部位被淬火有关.
对铁路车辆用耐候钢S450EW薄板进行了回火模拟试验,并进行力学性能测试,同时结合扫描电镜(SEM)、金相显微镜(OM)对显微形貌进行分析。研究回火工艺对S450EW钢板力学性能的影响规律,以及对S450EW组织的影响。研究发现,经工艺参数优化,随回火温度的提高,试验钢的强度下降,屈强比下降;钢的屈强比与组织中软硬相的强度差有关,强度差越大时,屈强比越低,在本组试验中,回火前的组织较为单一,基本以
利用RTW-10熔体综合物性测定仪,采用内柱体旋转法测量Cr2O3含量对CaO-SiO2-MgO-Al2O3-Cr2O3渣系的黏度及熔化性温度的影响,并利用FactSage热力学计算软件分析CaO-SiO2-MgO-Al2O3-Cr2O3渣系的相图。实验结果表明,固定高炉渣碱度为1.11时,随着炉渣中Cr2O3含量的增加,炉渣黏度下降,炉渣熔化性温度升高。当Cr2O3含量为1％～3％时,炉渣熔化性
Coal combustion is divided into two stages.One is the emission and combustion of volatiles and the second is the combustion of coal char.In this paper,effects of CaO on structure evolution and combust