【摘 要】
：
The combined addition of molybdenum and niobium is usually applied in fire-resistant steels with appropriate controlled rolling and controlled cooling.In order to develop new alloying strategy based o
【机 构】
：
Kunming University Of Science & Technology Kunming 650093 Yunnan China;Panzhihua Group Research Inst
论文部分内容阅读
The combined addition of molybdenum and niobium is usually applied in fire-resistant steels with appropriate controlled rolling and controlled cooling.In order to develop new alloying strategy based on the advantage of vanadium resource at Panzhihua Iron& steel(group)Co.,research on the Vanadium-containing fire-resistant weathering steels are conducted in this paper.Methods such as electron microscope,phase analyzing,tensile test,three dimension atom probe and so on were used to investigate the effect of vanadium on microstructure and tensile properties at both room temperature and high temperature up to 600℃ for different processes.The relationship between the microstructure and properties was analyzed.It has been found that the amount of vanadium precipitates would be raised as vanadium content rose.Adding vanadium into the steel was effective to increase the room temperature and elevated temperature yield strength,especially increased the content of nitrogen.Vanadium mainly exists in the pro-eutectoid ferrite of the test steel,the "hidden" vanadium will precipitate from base microstructure when the temperature elevated to 600℃,simultaneously improve the elevated temperature properties.The alloying strategy of fire-resistant weathering steels at Pangang Steel is ascertained through the experimental work.The study offers the essential technical support for the further development of products.
其他文献
本文利用武汉MST(Mesosphere-Stratosphere-Troposphere)雷达对降雨事件的观测,建立二阶高斯谱模型,拟合得到相应的大气湍流谱与降雨谱信息,从而提取大气背景三维风场及降雨参数信息,根据降雨回波谱反演不同高度的雨滴粒径分布.根据降雨回波信息特征及雨滴粒径伽马分布特征,研究了对流层区域降雨的微物理过程.
大气修正折射率剖面能够描述大气波导的特征,基于中尺度WRF模式,以NCEP再分析资料FNL数据作为背景场和边界场,采用二重嵌套,模拟了东海区域蒸发波导高度和强度分布,根据四参数蒸发波导M剖面模型建立M剖面,并与单参数蒸发波导M剖面和伪实测蒸发波导M剖面进行对比,结果发现和单参数模型相比,四参数模型可以更加灵活更加准确的描述蒸发波导M剖面.
Designing a competitive free-machining steel composition enabling less expensive steelmaking,manufacturing and recycling has long been a desirable objective.Foremost amongst a new approach has been si
Coal,as the most major energy in China,accounted for about 70%of Chinas primary energy production and consumption.While the percentage of coal as the primary energy mix would drop in the future due to
In this paper,different morphology and size of nano epsilon carbides(-carbides)were obtained by low temperature tempering for a low alloy abrasion resistance steel,the variation of mechanical properti
The CCT(continuous cooling transformation)curve of the test steel was obtained on Gleeble-1500 thermal mechanical simulator based on the thermal dilation measurement.The test steels were the deformati
The flow stress,microstructure and softening mechanism of NM550 wear-resistant steel were investigated via hot compression test by using Gleeble-1500 thermal simulator in a temperature range from 800
The chemistry composition,process parameters and the test results of Q890D free boron high strength steel plate used for engineering machinery was studied.The 16~40 mm thickness steel plates with good
Niobium Bearing Low Carbon Low Alloy(LCLA)value-added S355 structural steels reduces the overall material and construction costs for many high strength construction steel and heavy equipment applicati
It is well known that the strengthening mechanisms of Nb Microalloying on low carbon flat products have been widely studied and recognized since Microalloying 75 in Washington,DC,but the application r