Strain effect in epitaxial perovskite thin films

来源 :中国物理学会2011年秋季学术会议 | 被引量 : 0次 | 上传用户:liangjingyu1
下载到本地 , 更方便阅读
声明 : 本文档内容版权归属内容提供方 , 如果您对本文有版权争议 , 可与客服联系进行内容授权或下架
论文部分内容阅读
SrTiO3 (STO),and La1-xSrxMnO3 (LSMO) (x=0.17,0.33) thin films were epitaxially grown on (001),(110) and (100) NdGaO3 (NGO) substrates by pulsed laser deposition.Owing to relaxation of anisotropic misfit stress,crosshatch surface morphology were observed in STO/NGO systems.The crosshatch patterns exhibit characteristic surface undulation with ridge-like lines parallel to special crystallographic directions of the underlying NGO substrates.
其他文献
会议
会议
会议
会议
会议
The rectification effects in the systems based on quantum dots have attracted many researcherseyes.It was found that by changing the electric bias applied to a NM-QD-FM system,the current polarization
随着球差矫正器的应用,透射电子显微镜的分辨率已达到原子量级.然而,由于入射电子和样品间的相互作用,样品在观察过程中的不稳定性极大的限制了高分辨率的实现.因此,如何保持原子尺寸的样品在观察过程中稳定,是最终实现原子级分辨率首先需要解决的问题.
会议
本文研究了以碳纳米管作为燃料电池催化剂载体的新技术,其电催化性能要优于以活性炭或炭黑为载体的催化性能.采用镍基底上化学镀铁制备催化剂,利用CVD 方法制备多壁碳纳米管,经亲水处理后制成浆料.