【摘 要】
：
Selective acid Leach and beneficiation process was carried out to recover gallium from slag containing gallium.The experiment results of acid leaching tests showed that the leaching rate of Ga, A1 and
【机 构】
：
School Of Metallurgy and Environment Central South University ChangSha,HuNan,410012;Zijin Mining Gro
【出 处】
：
The 6th International Conference on Hydrometallurgy(第六届国际湿法冶
论文部分内容阅读
Selective acid Leach and beneficiation process was carried out to recover gallium from slag containing gallium.The experiment results of acid leaching tests showed that the leaching rate of Ga, A1 and K in the slag were above 83%,58% and 92% respectively, while the slag was leached with the liquid-solid ratio of 4:1,under that temperature of 80℃ for 2 hours.Results of selective concentration tests for gallium in solution showed that over 97% of gallium was precipitated, forming sediment containing a grade of over 4100g/t under the conditions that temperature was 80℃, leaching time length was 2 hours and pH was 2.4-2.6.On the other hand, with the same circumstances the precipitation rate orAl and K were respectively less than 20% and 1%, showing a different sedimentation behavior.
其他文献
Tropospheric delay is a major error source in geodetic techniques.In recent years,the Numerical Weather Models(NWMs),such as the European Centre for Medium Range Weather Forecasts(ECMWF),have been inc
The medium and short-term stability of hydrogen clocks and the medium and long-term stability of cesium clocks combine into a time-keeping clock set.This is a common practice in major time-keeping lab
建立了对铌铁合金采取化学溶解、浓缩制成熔片后应用X射线荧光光谱法测试铌铁中Al、Ti、Ta、V、Fe、Cu、Mn、Cr、Pb、Sn等成分的快速分析方法.讨论了各校正方式对测试结果的影响.结果表明,内标元素的加入对Nb的测试结果准确度并未带来改善,散射线的应用对于低含量重元素的测试效果也不理想,以理论α系数法校正基体效应,有效克服了铌铁中各元素谱线重叠与吸收增强效应的影响.
通过使用手持式X射线荧光光谱仪对铅锌矿含量进行分析,建立了矿山现场测定铅锌矿中Pb、Zn、Cu、Mo等元素的分析方法.针对现场测定铅锌矿的特点,选择直接粉末法进行检测.优化了电流、电压对测定的影响,比较了Ti、Ni等滤片的测试效果,对不同样品间的颗粒效应进行了校正.
本文从样品的分解处理、方法选择、指示剂选择等多方面进行验证得出,测定钙、镁元素使用盐酸分解样品,氨水沉淀干过滤进行测定;测定铝用硝酸、氢氟酸、高氯酸处理试样,碱分离进行络合滴定,标准偏差(SD)小于0.5％,相对标准偏差(RSD)均小于5.0％,加标回收率在96％～103％之间,弥补了此试样在没有国家标准指导的问题,解决了实验室自身分析难题,保证生产的有序进行,该方法单独作为进厂铝镁钙合金的元素检
监测力学试验设备使用全生命周期的稳定性对于保证测量结果的可靠性至关重要,大批量制作的有相同标称值的无时效力学标样是监测力学试验设备长期稳定性和评估设备系统偏差的有效工具.
为了分析PC钢绞线拉伸性能不合原因,采用扫描电镜、金相显微镜和电子探针配合波谱仪对断裂试样进行了断口观察、纵截面裂纹和组织分析、横截面碳元素面分析.分析结果表明:造成PC钢绞线拉伸试验性能不合原因是试样心部存在网状渗碳体,在拉拔过程中形成人字形裂口,裂口不断扩展,造成钢绞线未达到额定的最大力即发生提前断裂.
电池壳表面微小点缺陷特别是疑似"砂眼"缺陷已成为制约其产品质量的最重要因素.运用扫描电镜、光学显微镜、聚焦离子束等电子显微法和电解酸蚀法等电化学方法对电池壳表面常见的几类典型点缺陷表面、截面进行失效分析.
采用SE(B)试样进行KIC试验,通过金属材料平面应变断裂韧度方法中的GB/T4161-2007和TB/T 3276-2011两种标准辨别KQ的有效性,并对比分析两种标准在KQ有效性判定上的不同.
W and Mo existed in the form of peroxytungstic acid(H4W4Ol2(O2)2) and peroxymolybdic acid (H4Mo4O12(O2)2) in the presence of H2O2, since the chelating effect of H2O2retard the formation of isopolyions