The rhombohedral structure of graphite was widely considered as a mosaic distribution in a hexagonal host and was probably produced only by mechanical shear or milling.In this presentation, graphite b
【机 构】
：
Shenyang National Laboratory for Materials Science,Institute of Metal Research,Chinese Academy of Sc
【出 处】
：
第二届中国国际复合材料科技大会 (CCCM-2)
论文部分内容阅读
The rhombohedral structure of graphite was widely considered as a mosaic distribution in a hexagonal host and was probably produced only by mechanical shear or milling.In this presentation, graphite blocks were produced from mixture of natural graphite flakes, mesophase pitch and relevant dopants of Si and Ti powders by heating 30min at 2700oC and then pressing under the pressure of 30 MPa.
其他文献
为了解决陶瓷基复合材料工程结构件热强度评价问题，以连续纤维增韧的2D-C/SiC复合材料力学试验数据为基础，开展了面向工程应用的宏观唯象非线性本构建模研究。引入非弹性应变，对材料在力学试验中所体现的加载非线性、卸载模量衰减、拉压模量不对称等力学行为进行了建模。基于本文所提出的用于表征应力应变关系的指数形式本构方程所得的结果能与试验数据吻合良好。将所发展的力学模型与Tsai-Wu等失效模型相结合，完
发展先进高性能航空发动机是我国重大战略需求之一，航空发动机的性能以及可靠性问题已经严重制约了我国航空装备工业的发展。随着先进航空发动机技术的发展，对发动机性能指标要求不断提高，使得发动机热端部件如燃烧室、涡轮叶片和尾喷管等高温结构工作环境更加恶劣。对热端部件高温工作能力的要求已经超过了目前高温金属材料的温度使用极限，使得对高性能复合材料的需求日益迫切。
本文基于溶胶凝胶法,以硝酸镧硝酸锶硝酸锰为主要反应原料,以柠檬酸为螯合剂,制备了钙钛矿型锰酸锶镧陶瓷粉体,结合通过丝网印刷工艺,将粉体制备的复合浆料通过丝网印刷的方法印刷到氧化铝陶瓷板上,并采用不同的烧结温度1000℃,1100℃,1200℃,1300℃烧结成锰酸锶镧陶瓷薄膜。通过扫描电镜SEM,XRD扫描,和差热分析等手段研究了不同烧结温度对陶瓷薄膜的形貌和相结构的影响,并通过四探针电阻仪测量不
炭气凝胶复合材料由于具备轻质、耐高温、热导率低且良好的力学性能等优点，极具潜力作为新型高性能隔热材料应用于现代航天和工业等领域。传统的炭气凝胶隔热复合材料的制备工艺以水为溶剂，干燥之前需要经过溶剂置换过程，制备周期长。本文以异丙醇(Ⅰ)为溶剂，六次甲基四胺(H)为催化剂，配制间苯二酚(R)-糠醛(F)的醇溶胶，然后浸渍纤维预制件，经凝胶老化、超临界干燥、炭化制得炭纤维增强炭气凝胶复合材料，省却了置
采用真空等离子体喷涂技术制备超高温ZrB2基复合涂层,研究了该复合涂层的相组成和显微结构特征；研究了第二相,包括SiC、Si、MoSi2和TaSi2等,对该复合涂层的高温抗氧化性能的影响和作用机制。采用高温等离子体火焰表征了该复合涂层的抗烧蚀性能。实验结果表明,经过工艺优化ZrB2基涂层的气孔率可小于5％；含硅第二相的加入可以显著提高ZrB2基涂层的高温抗氧化性能；随着第二相含量的增加,ZrB2基
With the purpose of increasing application value and revealing the ballistic mechanism of ceramic matrix composites, it is necessary to investigate dwell phenomenon and ballistic performance of the ma
ZrB2具有优良的物理特性和化学稳定性而应用于许多领域，为了改善ZrB2难以烧结致密化和高温易氧化，本文通过共沉淀法制备包覆式Al203-Y203/ZrB2复合粉体，并对其进行放电等离子烧结制备ZrB2陶瓷基复合材料，研究增强相对ZrB2陶瓷基复合材料性能的影响。通过研究表明：两种包覆型粉体在700～1000℃时出现一次大的收缩，然后出现一个不收缩的平台阶段，两种包覆型粉体当温度达到1000～16
A precursor was synthesized through the reaction of Cp2ZrC12 and Ph2(NH3)2 and the pyrolyzed ceramics were characterized.The obtained precursor has a backbone with Zr-N-Ph unit and a relatively good s
Ni catalyst nanoparticles were deposited on SiC fiber surfaces inside three dimensional SiC fiber fabrics using four methods: vacuum impregnation, homogeneous precipitation, electrodeposition and auto
The results of work on the development of abrasive superhard composite materials based on diamond and cubic boron nitride due to structuring the powder material by carbon binder at subatmospheric pres