【摘 要】
：
In the present work, 06Cr19Ni10/Q235 clad composite materials are selected as the target materials.Then the deformation behavior, the surface deformation and damage characteristics of these samples we
【机 构】
：
Faculty of Materials Science and Engineering,Kunming University of Science and Technology,Kunming 65
【出 处】
：
第二届中国国际复合材料科技大会 (CCCM-2)
论文部分内容阅读
In the present work, 06Cr19Ni10/Q235 clad composite materials are selected as the target materials.Then the deformation behavior, the surface deformation and damage characteristics of these samples were considerably examined at different conditions (e.g.stain rate, loading direction, cladding ratio, and so on).
其他文献
本文采用单向冷压、烧结和热挤压方法制备30％(质量分数)SiCp/Al-Si基复合材料,利用SEM、XRD、拉伸强度等测试方法研究了不同时效温度对SiCp/Al-Si复合材料微观组织及力学性能影响规律.结果 表明：复合材料在500℃+4h固溶处理后,180℃时效6小时,Si相析出数量达到极值,材料强度达到最大值285MPa.随着时效温度的增加,析出相颗粒尺寸增大,材料的延伸率下降；断口韧窝增大,试
采用粉末冶金法制备了体积分数不同的微米碳化硅颗粒和纳米碳化硅颗粒混杂增强的铝基复合材料,采用扫描电镜和透射电镜对复合材料的微观组织进行表征,并对复合材料的拉伸性能进行测试,分析球磨混粉工艺参数对复合材料组织与性能的影响。结果 表明：碳化硅含量为10％,微纳米颗粒含量比为5∶1,球磨时间为8h的复合材料中微纳米碳化硅颗粒分布均匀,并与基体合金的界面结合良好。与粉末冶金法制备的基体合金相比,混杂增强复
采用搅拌摩擦加工技术制备了多壁碳纳米管增强铝基(MWCNTs/Al)复合材料,研究了碳纳米管含量对复合材料力学性能的影响规律.结果 表明：MWCNTs的添加对铝基复合材料的力学性能作用明显,随着MWCNTs含量的增加,MWCNTs/Al复合材料的硬度、弹性模量、强度都逐渐提高；当碳纳米管含量为6.6Vol.％时,复合材料强度达218MPa,为基体材料的2.24倍；随MWCNTs含量的增加,MWCN
W fiber reinforced copper materials fabricated by combustion synthesis melt infiltration under ultra-high gravity.Two styles for W fibers were designed.One is disordered stacking.Another is ordered ar
In this paper, the molybdenum coating was successfully deposited on the surface of diamond particles by direct current magnetron sputtering method, its surface morphology and chemical composition were
The mass fraction of 30% SiC particles reinforced Al-Si matrix composite was prepared by One-way press method, sintering and hot extrusion.The microstructure and mechanical properties of SiCp/Al-Si ma
碳/酚醛复合材料主要用于钝头体高超声速飞行器热防护，其冗余设计对于飞行器的质量控制有关键作用，因此准确预报其烧蚀行为能够解决热防护层设计过度冗余或可靠性不足的问题。本文对碳/酚醛复合材料在典型服役环境下的体积烧蚀机理、多物理场耦合过程进行了研究，并利用有限元方法实现了对中低热流、中等焓值对流热流载荷作用下材料的温度场、孔隙压力、材料热解程度以及力学响应的预报。为具有长时间大面积热防护需求的高超声速
Foam material could absorb more energy during the impact event.Compared with common materials, foam-core filled sandwich structures have better anti-impact properties.As the facesheet used in sandwich
The accelerated salt spray test was used to simulate the marine environment, and the effect of salt spray on flexural properties of glass fiber reinforced polyester (GFRP) composites was investigated.
为了研究碳化硅颗粒(SiCp)尺寸和体积分数对中体积分数SiCp增强铝基复合材料的导热系数的影响,用粉末冶金工艺制备体积分数为30、35和40 vol％,颗粒尺寸为3、8、15、25和40μm的SiCp/2024Al复合材料,利用SEM,激光导热仪等对材料微观结构和导热性能进行了研究。结果 表明,改变SiC颗粒的体积分数和尺寸能有效调节复合材料的导热系数。