【摘 要】
：
Recent advances in the photovoltage and thermoelectric material synthesis and characterization have engendered significant interest in their solar energy harvesting.However,examples of full-solar spec
【机 构】
：
School of Materials Science and Engineering,Beihang University,Beijing,100191
【出 处】
：
第十四届全国青年材料科学技术研讨会
论文部分内容阅读
Recent advances in the photovoltage and thermoelectric material synthesis and characterization have engendered significant interest in their solar energy harvesting.However,examples of full-solar spectrum energy harvesting in a single cell are relatively rare,and at present there are no known examples to solve the heat problem in conventional solar cell.Here we show that a synergistic photovoltaic and thermoelectric effect takes place in a single heterojunction solar cell that consists of a p-type CdTe nanorod array and n-type Bi2Te3 nanostructures.This novel cell is capable of converting light and heat into electricity via combined photovoltaic and thermoelectric processes,providing a simple and elegant material structure for development of high efficiency solar cells which can harvest solar energy over a wider solar spectrum.In addition,this discovery may provide a viable solution to the heat problems in conventional solar cells.
其他文献
采用电子束蒸镀的方法制备Ti/HfOx/Pt器件.通过测量器件的I-V曲线,研究器件的阻变特性.结合X 射线光电子能谱和透射电子显微镜研究,分析Ti/HfOx/Pt器件的阻变作用机制.X射线光电子研究表明当器件处于高阻态时,Hf4+所占Hf元素含量的百分比由Ti/HfOx界面向HfOx/Pt界面递增；而在低阻态时, Hf4+所占Hf元素含量的百分比则无明显变化.由此可确定氧空位缺陷形成的导电细丝在
针对水解溶胶-凝胶还原氮化法制备TiN薄膜时,所需原料金属钛醇盐价格相对较高,且其水解过程不易控制等问题。本文以四氯化钛和无水乙醇为前驱体原料,按C/Ti摩尔比为12∶1引入碳源聚乙烯吡咯烷酮(PVP,分子量为1300000),采用工艺简单的非水解溶胶-凝胶碳热还原氮化技术,在流量为32ml/min高纯N2中,经1300℃碳热还原氮化5h,在石英玻璃基片上制备出金黄色光泽的TiN薄膜。利用XRD、
自旋电子学材料与器件是近年来发展起来的新兴学科方向,是继微电子、光电子材料与器件之后崭露头角、具有更为诱人发展前景的新型信息存储、处理和读出的材料与高新技术.磁性异质结是自旋电子器件的关键支撑材料.异质结界面的交换耦合效应虽然在磁随机存储器、磁性传感器和硬盘读头等器件中得到了广泛应用,但是作为一个典型的界面现象,它仍然是材料物理领域一个长期悬而未决的基本科学问题[1].最近,我们通过建立界面电子结
Graphene-based composites have great potential applications in lithium ion batteries(LIBs)due to the peculiar electronic properties and high theoretical capacities.Herein,we report a facile,one-pot,hy
本文根据“团簇+连接原子”模型[1]指导设计了三元低弹性模量-Ti合金[MoTi14]Zr1(Ti78.2Mo11.2Zr10.6wt.％)和[SnTi14]Mo1(Ti75.7Mo10.9Sn13.4wt.％)， 研究了[MoTi14]Zr1和[SnTi14]Mo1合金中第二相析出对弹性模量和力学性能的影响及其拉伸过程中合金组成相的变化.利用铜模吸铸快冷技术制备6 mm合金棒，在MTS810拉伸
基于Ginzberg-Landau理论及连续形核理论,采用相场法模拟了Fe-B二元非晶合金过冷熔体的凝固动力学过程,通过界定凝固过程中固相百分数0.15％作为可观测的结晶百分数,计算出温度-时间转变(TTT)曲线和临界冷却速度(Rc),并以Rc作为玻璃形成能力(GFA)的直接表征.通过相场法计算得到的Fe-25％B二元非晶合金的Rc为1.1141×109K/s,与实验理论值6.8×106K/s相比
相对于贵金属离子，过渡族金属离子具有更低的标准电极电势。因此，若要通过热溶剂还原法合成过渡族金属纳米颗粒往往需要更强的还原剂或者更高的温度。然而，这样强烈的反应条件容易使得纳米晶的尺度分布不均匀、形貌难控制。获得均匀的纳米颗粒一般要求混合溶液在某个温度发生瞬间的均匀形核以及随后的缓慢生长。此时，溶液中阴离子的作用显得尤为重要。我们知道，在一定温度条件下，阳离子的电极电势是与溶液中相应阴离子的种类有
双元金属纳米颗粒具有不同于块体合金或单组份金属纳米颗粒的独特物理化学性能[1,2].Ni-Au双元纳米颗粒由于其优异的催化、光学、磁学等性能,具有广泛的应用前景[3,4].本文以嵌入原子势为基础,采用分子动力学方法研究了在升/降温过程中,三种典型的不同原子比的Ni-Au纳米颗粒(Ni@Au、Au@Ni和合金化NiAu)结构演变过程和原子扩散行为.研究结果表明：在升温过程,相对Au@Ni和合金化的N
金属材料中局域的弹性应变会显著地改变它们的物理、化学和力学性能，因此在纳米尺度上精确地测量这种局域的应变和应力，对于理解材料结构和性能的相互关系至关重要。我们利用定量电子显微学方法，通过精确地测量原子间的距离，获得了材料中原子尺度的局域应变、应力分布。利用高分辨像模拟方法，研究了实际实验条件下成像参数对定量应变分析精度的影响。利用原位电镜实验，发现微小尺寸的金属是通过表面不连续地发射出不全位错来完