The degradation of Ni-rich cathode materials exposing in the air is an inherent issue for its large-scale application.
Recovery and improvement the electrochemical performances of degraded LiNi0.8Co0.15Al0.05O2 for lith
【摘 要】
：
The degradation of Ni-rich cathode materials exposing in the air is an inherent issue for its large-scale application.
【出 处】
：
河南省化学会2016年学术年会
【发表日期】
：
2016年10期
其他文献
Feasible synthesis of protein-incorporated zinc phosphate nanotubes and used as support for Pt nanop
会议
Because of low cost and easy preparation,biomass as carbon source has aroused researchers wide attention.The design towards multidimensional structure for application in high performance storage is gr
Mesoporous TiO2 nanoparticles terminated with carbonate-like groups:visible-light photocatalytic act
Mesoporous carbonate-doped TiO2 microspheres were synthesized by a simple "one-pot"solvothermal method.The diameter of the TiO2 microsphere could be varied from 0.2 μm to 1.5 μm by adjusting the amoun
会议
A new metal-free method for the synthesis of 3-fluoro-2-oxindoles was developed.2-iodo-2-fluoro-N-phenylacetamide was prepared from simple aromatic amines with ethyl bromodifluoraacetate under neat co
MnCO3 spheres were synthesized by a simple hydrothermal method using Mn acetate as precursor.X-ray diffraction,field emission scanning electron microscopy,transmission electron microscopy(TEM),and ene
PANI-assisted fabrication of NiCo2O4/PANI electrode material with enhanced performance for asymmetri
Herein,one of the most well-known conducting polymers,polyaniline(PANI)was coated onto NiCo2O4 nanosheet arrays through a facile hydrothermal synthesis method and an efficient physical blending proces
In order to improve the photocatalytic performance of TiO2,the research of doping and modifing with rare earth ion on nanometer TiO2 is widely attention.
With the development of flexible electronics,flexible supercapacitor shows great potential in the flexible display devices and flexible storage system.
In recent years,nickel and cobalt bimetallic compound materials as supercapacitors electrode materials have drawn great attentions by virtue of their enhanced electroconductivity and specific capacity