A process of the selective leaching of nickel from low-sulfur Ni-Cu matte at atmospheric pressure was described.This matte was obtained from high grade Ni-Cu mtte by magnetic separation, which mainly
【机 构】
：
School of Material & Metallurgy, Northeastern University, Shenyang, 110004, P.R.China
【出 处】
：
第五届国际湿法冶金学术会议(5th International Conference on Hydrometallurg
论文部分内容阅读
A process of the selective leaching of nickel from low-sulfur Ni-Cu matte at atmospheric pressure was described.This matte was obtained from high grade Ni-Cu mtte by magnetic separation, which mainly contained Ni-Cu alloy and a small quantity of sulfides.Firstly, the acid-oxygen (CuSO4-H2SO4-O2) leaching of the matte was conducted at atmospheric pressure.When the solution pH value reached 1.0 ~ 2.0, the oxygen flow was ceased.Then the aqucous copper was rejected by cementation reaction with Ni in the alloy.The mineralogical characteristics of the matte in the process were analyzed by X-ray diffraction, optical microscopy and scanning electron microscopy.And the effects of variations in temperature, particle size distribution, oxygen flow rate, pulp density, initial acid concentration and initial concentration of copper ion were investigated.
其他文献
For purpose of deeply depositing silica from high concentration of sodium aluminum solution, it is put forward to the uses of new desilication agent-the ferrite series compound, i.e.Calcium Hydroferri
In this study nickel particles were prepared by spray pyrolysis of NiSO4·6H2O solution with hydrogen and/or other additives such as urea, ammonia.For each method of preparation we investigated the pro
Different TiO2 such as anatase, rutile and sintered C/anatase were added to magnesium hydride by high-energy ball milling in order to improve the hydrogenation properties of the magnesium hydride.The
The 0.1mol·L-1CuSO4 liquor and 4mol·L-1NaOH liquor were prepared by CuSO4·5H2O and NaOH as raw materials.The difform nano-CuO were prepared by hydrothermal decomposition method.The Fig.1(a) was TEM ph
Ti4+-mixed FePO4·xH2O precursor was prepared by co-precipitation method, for which Ti4+ cations were added in the process of preparing FePO4·xH2O to pursue a effective and homogenous doping way.Ti4+-d
Abstract A dual cell system with chalcopyrite anode and MnO2 cathode was used to study the relations between time and such data as the electric quantity and the dissolved rates of the two minerals in
The alterations of surface properties of pyrrhotite after biological conditioning with Leptospirillum ferriphilum and Acidithiobacillus caldus were evaluated by zeta-potential, adsorption and contact
Citric acid has been proved to be one of the most effective organic acids to extract Nickel selectively from laterite ores.Less attention has been paid to cobalt recovery compared to nickel recovery i
A dual cell system was used to study the electrogenerative leaching sphalerite-MnO2 under the conditions of presence and absence of Acidithiobacillus thiooxidans (A.thiooxidans).The polarization of an
Molybdenite is the source material for the processing of molybdenum.There are several schemes for molybdenite processing , including hydrometallurgieal methods based on leaching by nitric acid1 or pyr