The effects of solution and aging treatments on the microstructure evolution and mechanical properties of the as-cast Mg-6Zn-1.4Y-0.6Zr alloy were investigated.The results indicate that the solution t
【机 构】
：
State Key Lab of Materials Processing and Die & Mould Technology, Huazhong University of Science and
【出 处】
：
2016中国有色合金及特种铸造发展论坛(第3届有色合金及特种铸造技术国际研讨会、第十一届中国国际压铸会议、第九届中国铸造
论文部分内容阅读
The effects of solution and aging treatments on the microstructure evolution and mechanical properties of the as-cast Mg-6Zn-1.4Y-0.6Zr alloy were investigated.The results indicate that the solution treatment can obviously dissolve the net-like intermetallic compounds (mainly I-phase) into the α-Mg matrix.Meanwhile, the I-phase decomposes gradually above 440 ℃, with the formation of fine W-phase and Mg7Zn3 phase.Further aging treatment results in the precipitation of numerous fine and dispersive particles in the α-Mg matrix.The best mechanical properties of the heat treated alloy are obtained after solution treated at 460 ℃ for 8 h and aged at 200 ℃ for 16 h, with the yield strength (YS), ultimate tensile strength (UTS) and elongation are 208 MPa, 257 MPa and 3.8%, respectively.Compared with the as-cast alloy, the increment of YS and UTS are 117% and 58% respectively, while the decrement of elongation is 46%.
其他文献
目录Contents 1 问题的提出2 悬浮态磁化焙烧-磁选小型试验3 实验室扩大试验研究4 半工业试验5 60万吨/年工业试验6 结语Part 1问题的提出1 问题的出现状我国铁矿石资源量680亿吨(2008年统计数据),但禀赋差、含铁量低.入选 铁品位逐年下降,选矿比逐渐提升.
基于介质碰撞模型研究了搅拌叶轮转速、矿浆浓度和介质类型对GN8型搅拌磨机能量利用率的影响.研究发现,在矿浆浓度相同的情况下,搅拌叶轮转速为1160r/min的能量利用率低于转速870r/min时,这与介质的类型关系不大.在搅拌叶轮转速相同的情况下,矿浆浓度为40％时,刚玉球作为磨矿介质的能量利用率高于氧化锆球作磨矿介质的情况,在矿浆浓度为60％时,恰好相反.在磨矿过程中,增加矿浆浓度,是否有利于磨
针对页岩钒行业中有害气体多污染物排放、废水氨氮大幅超标、尾渣堆存隐患等突出问题,分析了目前我国页岩钒行业整体环境现状,介绍了基于全过程污染防治的页岩钒清洁生产新技术.通过云母类矿物焙烧过程的结构重建式转变,高效缓释助浸剂强化浸出效果和降低酸耗等措施,从源头上实现有害气体减排和废水氨氮减量.通过钒尾渣低稳态非晶化和"—SiO4—AlO4—"三维网络重构,制备出综合性能优于硅酸盐水泥的地聚物新材料,实
对闪速磁化焙烧装置的最佳给矿粒度进行了研究,表明在反应炉温度(750±30)℃、CO浓度0.16％～0.40％条件下,在0.1～0.5mm范围内,随着给料粒度变粗,焙烧矿磁化转化率降低;对于0～0.1mm粒级矿样,因细粒级磁化时磁性主要是由磁畴的转动产生,所需的能量比磁畴壁的移动大得多,因而细粒级焙烧矿的弱磁选效果相对粗粒级差,综合考虑,闪速磁化焙烧装置的最佳给料粒度为-0.3mm.-0.3mm的
对万宁市某海滨砂矿进行了工艺矿物学和钛铁矿选矿试验研究.结果表明:在原矿TiO2含量11.79％时,采用内筒式永磁-湿式弱磁-电选新工艺流程,可得到TiO2含量49.50％、回收率为69.27％的钛铁矿精矿(含部分钛铁矿蚀变的金红石),为该类型海滨砂矿中钛铁矿的综合回收利用提供了技术依据.
For primary aluminum producers the largest amount of energy used in the manufacturing process is consumed by the electrolytic process, 63%;an additional 23% is used in process heating.For the secondar
For further expansion of aluminum usage to the area where heavy dynamic loading is required in vehicles, improvement on as-cast properties of aluminum alloys and their corresponding manufacturing proc
The effects of pre-aging of RRA treatment on microstructure, mechanical properties,intergranular corrosion (IGC) and exfoliation corrosion (EXCO) behavior of spray formed 7075 aluminum alloy were inve
金属熔体均细处理技术(或称外场处理技术)是金属熔体处理技术的重要类别之一,它应用于金属半固态或低温液态流变成形等各种铸造场合,目的是实现凝固组织的整体均匀化和细化.基于性价比,本文提出了评价外场处理技术的三个原则:工艺简单原则、均匀细化原则和减少缺陷原则.结合对现有外场处理技术的客观评价,引荐了一种类似豆浆机原理的"金属熔体切割破散处理技术".
阐述了机器人打磨及其自动化应用在汽车发动机铝合金缸体、缸盖后处理方面的优势及应用.通过机器人实现对专用设备(如:锯床、震沙机、机加工)的整合,借助3D视觉等手段通过机器人完成转运箱取件及装箱实现自动化物流,借助视觉缺陷识别技术实现在自动化物流阶段的视觉检验,透过MES系统实现铸造、后处理及自动化物流的生产信息收集及管理.