Effect of cooling rate on microstructure and compressive performance of AZ91 magnesium alloy

来源 :Transactions of Nonferrous Metals Society of China | 被引量 : 0次 | 上传用户:never0005
下载到本地 , 更方便阅读
声明 : 本文档内容版权归属内容提供方 , 如果您对本文有版权争议 , 可与客服联系进行内容授权或下架
论文部分内容阅读
<正>Effect of cooling rate on both microstructure and room temperature compressive performance of the AZ91 magnesium alloy was investigated. The experimental results show that with increasing cooling rate, the quantity of the solid solution phase inc
其他文献
目的:探讨干细胞移植辅助丝裂霉素C(MMC)治疗翼状胬肉的效果.方法:初发性胬肉20例、26眼于显微镜下彻底切除胬肉组织,干细胞移植辅助MMC治疗.结果:术后20例、26眼4~6d角膜上皮
Based on Kohler&#39;s ternary solution model and Miedema&#39;s model for calculating the formation heat of binary solution, the integral equation was establishe
<正>Age hardening characteristic and tensile property of Mg-3.5Dy-4.0Gd-3.1Nd-0.4Zr alloy were investigated. The alloy exhibits a considerable age hardening eff
Tensile properties, fracture characteristics and microstructures of 7055 aluminum-based alloy containing Ag after T6, T73 and RRA treatment were investigated. T
The microstructures and damping capacity of AZ91D cast alloys containing various Ce contents were investigated. Damping capacity (Q-1) of the alloys was measure
目的:观察治疗急性视网膜坏死综合征(ARNS)的临床疗效.方法:回顾分析急性视网膜坏死综合征12例、17眼的临床资料,包括临床表现、辅助检查(荧光素眼底血管造影、视网膜电图)以