乙二胺四乙酸二钠对镍钛合金表面电沉积羟基磷灰石涂层的影响

来源 :电镀与涂饰 | 被引量 : 0次 | 上传用户:flypoet
下载到本地 , 更方便阅读
声明 : 本文档内容版权归属内容提供方 , 如果您对本文有版权争议 , 可与客服联系进行内容授权或下架
论文部分内容阅读
先用10mol/L的NaOH溶液处理镍钛片,随后采用电沉积法制备羟基磷灰石涂层。电沉积工艺参数为:硝酸钙0.042mol/L,磷酸二氢铵0.025mol/L,EDTA-2Na1.5×10-4mol/L,温度65℃,pH4.5,电流密度1mA/cm2,时间1h。采用扫描电镜、红外光谱仪和能谱仪对所得涂层进行表征。NaOH溶液处理有利于羟基磷灰石的生长。溶液中EDTA-2Na的存在不影响羟基磷灰石的生成,只是促使羟基磷灰石末端聚拢,使羟基磷灰石之间的空隙扩大,并减少涂层的CO3-2含量,增加OH-,有效减少了涂层的镍含量。 Nickel-titanium sheets were first treated with 10 mol / L NaOH solution and then hydroxyapatite coatings were prepared by electrodeposition. The parameters of electrodeposition were 0.042mol / L of calcium nitrate, 0.025mol / L of ammonium dihydrogen phosphate and 1.5 × 10-4mol / L of EDTA-2Na, the temperature was 65 ℃, the pH was 4.5, the current density was 1mA / cm2 and the time was 1h . The resulting coating was characterized by scanning electron microscopy, infrared spectroscopy and energy dispersive spectroscopy. NaOH solution is conducive to the growth of hydroxyapatite. The presence of EDTA-2Na in the solution did not affect the formation of hydroxyapatite, but prompted the end of hydroxyapatite gather, the gap between the hydroxyapatite expanded, and reduce the coating CO3-2 content, increase OH-, Effectively reduce the nickel content of the coating.
其他文献
回 回 产卜爹仇贱回——回 日E回。”。回祖 一回“。回干 肉果幻中 N_。NH lP7-ewwe--一”$ MN。W;- __._——————》 砧叫]们羽 制作:陈恬’#陈川个美食 Back to yield
随着我国高职教育事业蓬勃发展,高职院校会计作为对高职院校各项事业和业务活动进行确认、计量和记录,并将记录的结果报告给相关信息使用者的信息系统,也逐渐引起了人们的重
目的:分析小儿轮状病毒(rotavirus,RV)肠炎并发心肌损害(myocardial damage,MD)的危险因素,以指导临床诊疗。方法收集207例RV肠炎患儿的临床资料,对可能导致MD的变量进行单因素及多因
目的了解研究在对中老年牙周病患者进行临床治疗时,应用中医药治疗方法的治疗效果与应用价值。方法对2018年1月~2019年4月在某院口腔科进行诊疗的中老年牙周病患者的诊疗信息
在企业追求竞争优势地位、科学管理及资源优化配置的过程中,全面预算管理应运而生。它的产生是生产力发展与管理科学化的集中体现。中兴智能交通有限公司也实行了全面预算管
职业教育的发展已为国家现代化建设培养了大批的高素质人才,有力地推动了经济发展和社会进步,并且它在改变“学而优则仕”的传统教育观念,在促进人的个性发展和全面素质提高
传统英语听力课堂只重视语言知识的掌握,忽视背景知识的重要性,导致学生缺乏相关图式而听力水平难以提高。基于图式所构建的英语专业听力教学模式,听前激活图式,听中运用图式,听后
<正>采访手记:十二年前的那个春天,《资源再生》杂志社的同仁作为环境保护部的课题组成员,参加了《长江三角洲地区再生金属产业现状调查及前景分析预测》的调研,第一站就来到