Nano-sized amorphous Al 2 O 3 -2SiO 2 powder was prepared by a sol-gel method coupled with azeotropic distillation. The structure of the powder was investigated by DTS, BET, TEM, FT-IR, TG-DTA and XRD, showing that n-butanol azeotropic distillation could effectively remove water from the aluminosilicate gels and prevent the formation of hard agglomerates in the drying process. The average particle diameter of the powder was about 70 nm. The largest BET specific surface area of the powder was 669 m 2 /g. To examine the alkali-activation reactivity of the powder, alkali-activation tests were performed with the powder reacting with sodium silicate solution. The synthetic powder was found to be highly reactive.
Nano-sized amorphous Al 2 O 3 -2SiO 2 powder was prepared by a sol-gel method coupled with azeotropic distillation. The structure of the powder was investigated by DTS, BET, TEM, FT-IR, TG-DTA and XRD, showing that n-butanol azeotropic distillation could be effectively remove water from the aluminosilicate gels and prevent the formation of hard agglomerates in the drying process. The average particle diameter of the powder was about 70 nm. The largest BET specific surface area of the powder was 669 m 2 / g. To examine the alkali-activation reactivity of the powder, alkali-activation tests were performed with the powder reacting with sodium silicate solution. The synthetic powder was found to be highly reactive.