Anodizing of AZ31 Mg alloy in NaOH solution by co-precipitation of cerium oxide was investigated.The chemical composition and phase structure of the coating film were determined via optical microscopy,SEM and XRD.The corrosion properties of the anodic film were characterized by using potentiodynamic polarization curves in 17 mmol/L NaCl and 0.1 mol/L Na2SO4 solution at 298 K.The corrosion resistance of AZ31 magnesium alloy is significantly improved by adding cerium oxide to alkaline solution.In addition,the surface properties are enhanced and the film contains no crack.
Anodizing of AZ31 Mg alloy in NaOH solution by co-precipitation of cerium oxide was investigated. The chemical composition and phase structure of the coating film were determined via optical microscopy, SEM and XRD. The corrosion properties of the anodic film were characterized by using potentiodynamic The polarization curves in 17 mmol / L NaCl and 0.1 mol / L Na2SO4 solution at 298 K. The corrosion resistance of AZ31 magnesium alloy was significantly improved by adding cerium oxide to the alkaline solution. In addition, the surface properties are enhanced and the film contains no crack.