The application of ‘extreme’ hydrogen-decrepitation (HD) process using high-pressure disproportionation was extended to Sm-Co5-type-alloy. The alloy with nominal composition of Sm36Co64 was treated under 1.0~2.0 MPa H2 pressure for several hours at room t