一、绪言已研究出了好几种生产具有良好延展性的高强度双相钢的生产方法。生产热轧双相钢有两种方法:(1)在相当高的温度下进行卷取,这些钢含有很高的 Mn、Cr 或者 Mo(2)在低温(≤400℃)下卷取,这些钢含有少量的添加元素。
I. INTRODUCTION Several production methods have been developed for the production of high strength duplex steel with good ductility. There are two ways to produce hot-rolled dual-phase steels: (1) Coiling at fairly high temperatures with high Mn, Cr or Mo (2) coiling at low temperatures (≤400 ° C) Steel contains a small amount of added elements.
其他文献
BaGa4,tetragonal space group I4/mmm with lattice parameters a=b=4.5650(8), c=10.786(2)A, V=224.77(7)A3,Dc=6.15 gcm-3,and Z=2,λ(MoKα)=0.71069A,μ=335.93cm-1,F
The reaction of vinylmagnesium bromide (1) with trityl chloride (2) was investigatedand the products were identified as triphenylmethane (3) (81%), acetylene (
C19H14N2O2ClSSb,Mr = 491.6, space group P1, a = 5.977(1), b= 8.708(1), c = 8.962(1) X, a=93.91(1),B= 103.25(1),r=94.80(1), V = 450.6 A3, Z = 1, Do = 1.79, DC =
苍山洗马潭位于苍山玉局峰和龙泉峰顶的交接处,海拔3920米,被称为“山巅之湖”。洗马潭面积约4500平方米,潭深约1.5米,属第四纪大理冰期高山冰碛湖。有年代资料显示,其地质年
利用真空石英管法在890～1100℃合成新化合物Pr_3SbS_6的单晶,并测定了其晶胞参数.Pr_3SbS_6为四方柱体、红色透明结晶,属于四方晶系,空间群为I4_1/acd,晶胞参数为a=15.506(7),
本文报告了DPS8计算机MNDO程序。由于DPS8机对每个用户的内存限制,所以已改造了原始MNDO 程序使适应于该机型。这个程序可用于优化分子几何和寻找限制性反应过度态。作为应用
请下载后查看，本文暂不支持在线获取查看简介。
Please download to view, this article does not support online access to view profile.
请下载后查看，本文暂不支持在线获取查看简介。
Please download to view, this article does not support online access to view profile.
这种扩孔钻用于精密深孔的扩孔加工。它以T15K6硬质合金刀片作刀头。加工过程中,刀具的导向由安装在切削刃后边的能自动调节的导向装置1来完成。这些导向装置组成了一个旋转
请下载后查看，本文暂不支持在线获取查看简介。
Please download to view, this article does not support online access to view profile.