Polyethersulfone (PES)-modified epoxy systems with stepwise reaction were studied throughout the entire curing process by using optical microscopes, time-resolved light scattering (TRLS), and a rheolometry instrument compared with that of chainwise polymerization. The results suggested that the phase separation process is mainly controlled by the diffusion of epoxy oligomers for stepwise mechanism system and by that of epoxy monomers for chainwise mechanism system. In case of high PES content (SPES-20%) light-scattering results showed a viscoelastic phase separation and the characteristic relaxation time of phase separation can be described well by the WLF equation. However, in the case of low PES content (SPES-14%) secondary phase separation phenomenon was observed by Optical Microscope and further demonstrated by rheological study.
Polyethersulfone (PES) -modified epoxy systems with stepwise reaction were studied throughout the curing process by using optical microscopes, time-resolved light scattering (TRLS), and a rheolometry instrument compared with that of chainwise polymerization. The results suggested that the phase separation process is mainly controlled by the diffusion of epoxy oligomers for stepwise mechanism system and by that of epoxy monomers for chainwise mechanism system. In case of high PES content (SPES-20%) light-scattering results showed a viscoelastic phase separation and the characteristic relaxation However, in the case of low PES content (SPES-14%) secondary phase separation phenomenon was observed by Optical Microscope and further demonstrated by rheological study.