摘要：这些年来，越来越多的建筑安装公司对大体积混凝土浇筑技术青睐有加，这主要得益于该浇筑技术的种种优势。本篇论文根据近十年的建筑施工领域的实践经验，简要介绍了大体积混凝土浇筑技术在领域内的应用中出现的一系列问题，并以此为根据，对建筑施工中大体积混凝土浇筑技术进行了深入，以使该技术在建筑施工中起到极佳的作用。
关键字：大体积混凝土浇筑技术；建筑施工；问题；分析和研究
These years, more and more construction and installation company has added to the favor of large volume concrete pouring technology, all sorts of advantages which is mainly due to the casting technology. In this paper, according to the construction area of nearly ten years of practical experience, introduces a series of problems about application of pouring technology for mass concrete in the field of, and on this basis, the pouring technology for mass concrete construction of in-depth, in order to make this technology play a great role in the construction construction
Keywords: pouring technology for mass concrete; construction; problem; analysis and research
中图分类号： TV544+.91文献标识码：A
在实际的建筑施工作业中，大体积混凝土的浇筑技术本质上和如何防止大体积混凝土出现裂缝的技术基本相同。接下来，为更深入地了解混凝土浇筑技术，我们着重研究如何增强混凝土极限抗拉强度，减慢混凝土温度下降的速率等技术。
1大体积混凝土浇筑常出现的问题
实际建筑施工中，进行大体积混凝土浇筑过程中，应对以下问题加以重视：
1.1施工中形成的冷缝。
冷缝实质上就是一种在实际大体积混凝土浇筑时出现的各种形状的质量缝，其形成的原因有两个，第一，现实中的种种情况使得混凝土得不到有效供应；第二，实际混凝土浇筑过程中，使用的一些方式方法不合理。这种问题往往存在于混凝土分层浇筑这一工序中，主要是由于两相邻混凝土分层浇筑的时间设置地不合理，如果在第一层混凝土的浇筑初凝时间大于第二层混凝土的浇筑时间，那么混凝土连续浇筑作业就难以取得预期的效果，冷缝的存在也就不可避免。这种问题就会使得两相邻混凝土层之间结合得不太好，从而造成大体积混凝土的质量严重下降。
1.2由于干燥收缩而引起的缝隙
大体积混凝土的浇筑往往使用泵送方法进行作业，这种方法使得混凝土中的水分相当多，含量较多的是游离水，等到混凝土变得坚硬之后，因为这种游离水的大量挥发，所以，混凝土就会变得非常干燥，与此同时也在不断收缩，又因为边界条件的限制和混凝土中存在的收缩变形，使得很凝土结构中出现了非常大的拉应力，如果混凝土自身的抗拉强度大于或等于这一拉应力，那么混凝土中就不会有裂隙出现，其结构是稳定的；否则，混凝土中就会出现裂隙，导致其结构受到严重的破坏。
1.3由温度因素而造成的裂缝
在混凝土不断变硬的过程中，混凝土内部会产生大量的热，却很难散发，从而使得其内部温度逐渐增加，再加上混凝土内部的散热速率远远小于其外部的散热速率，如此混凝土表里之间的温度就会存在一定的差值，从而造成混凝土表里分别承受着不同性质的应力，如果混凝土自身的抗拉强度小于这一温度应力时，混凝土中就极易出现此种裂缝。
1.4泌水现象
泌水现象指的是因为水泥有着极强的吸水性，而造成很多水从混凝土外部析出的现象。混凝土在浇筑过程中使用的水越多，且其温度越低，那么其析出的水分也就越多。此外，混凝土的析出水量还会受到水泥颗粒大小及其物质组成的影响。在混凝土分层浇筑过程中往往会出现泌水现象，分层作业的时间差的大小在此过程中对这一现象有着严重的影响，这一差值太大太小均不可以，如果这种时间差值设置地不合理，混凝土内部的起着粘结作用的应力显然不符合要求，泌水现象势必不可避免。
2探讨建筑施工过程中大体积混凝土的浇筑技术
本文在此之前已经论述了混凝土浇筑过程中存在的问题，下面本文将会深入探讨大体积混凝土的浇筑技术。根据近年来的建筑施工实践，我们总结出下面四个方面是研究混凝土浇筑技术的基础：第一，合理选择混凝土材料；第二，采用恰当的混凝土浇筑方式；第三，合理确定混凝土配合比例；第四，加强混凝土的温度控制及其养护。
2.1混凝土材料的选取应以遵循设计要求与规范为基础
第一，为更好地防止混凝土温度升高，需要采用低熱或中热水泥，从而可以使混凝土的温度应力符合相关要求。若建筑施工中选择强度等级合理的由某些成分组成的水泥材料，可以使其水化热得到有效控制，从而使得大体积混凝土温度升高的范围合理。第二，可以把一定量的粉煤灰放入混凝土。如果放入的粉煤灰量合理，其量为水泥量的三分之一至二分之一，如此方可更好地应用粉煤灰的某些性质，也就是所谓的滚球效应，这可以不仅可以提高混凝土的流动性，而且还可以增强器粘结性，此外，对于其水化热的控制也具有良好的效果。与此同时，把一定量的粉煤灰加入混凝土中，如此可以减少水泥的使用量，从而节约了生产费用。第三，在混凝土中加入一定量的相关增强剂。如此能够使得混凝土的水灰比控制在一定的范围，防止其收缩过大，优化其孔结构，增大其拉应力，甚至还能够改善混凝土的抗裂性及其抗渗性。第四，充分发挥混凝土后期强度的作用。根据丰富的建筑施工经验可知，为得到很好的混凝土后期强度，需把一定量的性能极好的粉煤灰放入混凝土中，在满足合理地水灰比条件下，可以是混凝土形成一个极好的强度增长，故而，大体积混凝土施工过程中往往选择一些高龄期的粉煤灰，才能获得合理的强度，如此能够减少水泥的使用量，还能够使混凝土温升得到有效的控制。
2.2以合理的方式方法进行混凝土浇筑
现如今，在建筑工程作业中，往往选择砖模或木模，以使得大体积混凝土外表的热挥发量降低。如果选择钢模的话，应注意其热挥发量的特殊情况，有可能造成混凝土表里存有较大的温差，因此，应选择相应的保温方法。进行大体积混凝土浇筑施工时，可按全过程设计要求，结合混凝土的相关特点，选择斜分层等形式，使混凝土厚度逐渐增加。
2.3合理确定混凝土配制比
合理的混凝土配制比可以使大体积混凝土的质量得到很好地提升。下面几个举措均可提高混凝土质量：合理确定水和水泥的量比，使得含泥量满足一定的范围，确定合理的骨料级配，提出相关方案，还需使得钢筋等不出现变动。在建筑施工中，往往使用泵送方式进行大体积混凝土浇筑，所以，合理确定配制比应满足减少水泥使用量和浇筑方法的要求。睡你的使用量不宜过多或过少，应确定在合理的范围。同时，砂率也应保证有合理的范围，应使石子的级配符合一定的要求。
2.4加强温控和养护数据搜集工作
处理好大体积混凝土的养护工作需要使混凝土的温度和湿度满足一定的要求，因此，应选择相关保温方法，以降低混凝土外部的热量挥发，减少其表里的温度差值，从而避免其产生裂缝。为使其温度得到更好地控制，需要选择科学的测温方法，这一工作应养护中做好，在混凝土浇筑工作结束后，就立即对其进行养护，其温度测量有两种方法，一是人工方法；二是计算机方法。此二种方可以同时使用在建筑施工中，也可任选一种。要视实际情况而定。
结束语
综上所述，进行好大体积混凝土浇筑施工绝非一项简单的事情，可谓是一个伟大的工程。在建筑施工中，对其质量产生不利影响的原因多不堪言，如果浇筑技术应用得不当，混凝土往往会存有较为严重的质量问题。故而，为使得大体积混凝土浇筑施工不受混凝土质量中出现的问题的影响，应找到合理的浇筑技术方法，以保证混凝土施工质量，从而获得较好的建筑施工质量。
参考文献
[1] 陈寰.对建筑施工中的混凝土浇筑技术探讨[J].价值工程,2011(03)
[2] 邓小钱.建筑施工中的大体积混凝土浇筑技术[J].中国水运(下半月),2009(03)
[3] 周安明,陈斌.对混凝土浇筑技术的探讨 [J].中国新技术新产品,2010(22)
[4] 李丽宏.“三掺技术”在大体积混凝土施工中的应用.民营科技.2008（02）
[5] 江正荣.建筑施工工程师手册［M］.北京：中国建筑工业出版社，2002（12）
[6] 孙修艾、程曙明.大面积框架结构梁板混凝土一次整体浇筑施工技术[J].建筑技术，2003（01）
[7] 李国胜.建筑结构裂缝及加固疑难问题的处理——附实例[M].北京：中国建筑工业出版社，2006.
[8] 迟陪云.大体积混凝土裂缝的起因及防治措施[J].混凝土，2001（12）
[9] 陈勇.混凝土浇筑技术措施[J].大众科技,2011(08)
关键字：大体积混凝土浇筑技术；建筑施工；问题；分析和研究
These years, more and more construction and installation company has added to the favor of large volume concrete pouring technology, all sorts of advantages which is mainly due to the casting technology. In this paper, according to the construction area of nearly ten years of practical experience, introduces a series of problems about application of pouring technology for mass concrete in the field of, and on this basis, the pouring technology for mass concrete construction of in-depth, in order to make this technology play a great role in the construction construction
Keywords: pouring technology for mass concrete; construction; problem; analysis and research
中图分类号： TV544+.91文献标识码：A
在实际的建筑施工作业中，大体积混凝土的浇筑技术本质上和如何防止大体积混凝土出现裂缝的技术基本相同。接下来，为更深入地了解混凝土浇筑技术，我们着重研究如何增强混凝土极限抗拉强度，减慢混凝土温度下降的速率等技术。
1大体积混凝土浇筑常出现的问题
实际建筑施工中，进行大体积混凝土浇筑过程中，应对以下问题加以重视：
1.1施工中形成的冷缝。
冷缝实质上就是一种在实际大体积混凝土浇筑时出现的各种形状的质量缝，其形成的原因有两个，第一，现实中的种种情况使得混凝土得不到有效供应；第二，实际混凝土浇筑过程中，使用的一些方式方法不合理。这种问题往往存在于混凝土分层浇筑这一工序中，主要是由于两相邻混凝土分层浇筑的时间设置地不合理，如果在第一层混凝土的浇筑初凝时间大于第二层混凝土的浇筑时间，那么混凝土连续浇筑作业就难以取得预期的效果，冷缝的存在也就不可避免。这种问题就会使得两相邻混凝土层之间结合得不太好，从而造成大体积混凝土的质量严重下降。
1.2由于干燥收缩而引起的缝隙
大体积混凝土的浇筑往往使用泵送方法进行作业，这种方法使得混凝土中的水分相当多，含量较多的是游离水，等到混凝土变得坚硬之后，因为这种游离水的大量挥发，所以，混凝土就会变得非常干燥，与此同时也在不断收缩，又因为边界条件的限制和混凝土中存在的收缩变形，使得很凝土结构中出现了非常大的拉应力，如果混凝土自身的抗拉强度大于或等于这一拉应力，那么混凝土中就不会有裂隙出现，其结构是稳定的；否则，混凝土中就会出现裂隙，导致其结构受到严重的破坏。
1.3由温度因素而造成的裂缝
在混凝土不断变硬的过程中，混凝土内部会产生大量的热，却很难散发，从而使得其内部温度逐渐增加，再加上混凝土内部的散热速率远远小于其外部的散热速率，如此混凝土表里之间的温度就会存在一定的差值，从而造成混凝土表里分别承受着不同性质的应力，如果混凝土自身的抗拉强度小于这一温度应力时，混凝土中就极易出现此种裂缝。
1.4泌水现象
泌水现象指的是因为水泥有着极强的吸水性，而造成很多水从混凝土外部析出的现象。混凝土在浇筑过程中使用的水越多，且其温度越低，那么其析出的水分也就越多。此外，混凝土的析出水量还会受到水泥颗粒大小及其物质组成的影响。在混凝土分层浇筑过程中往往会出现泌水现象，分层作业的时间差的大小在此过程中对这一现象有着严重的影响，这一差值太大太小均不可以，如果这种时间差值设置地不合理，混凝土内部的起着粘结作用的应力显然不符合要求，泌水现象势必不可避免。
2探讨建筑施工过程中大体积混凝土的浇筑技术
本文在此之前已经论述了混凝土浇筑过程中存在的问题，下面本文将会深入探讨大体积混凝土的浇筑技术。根据近年来的建筑施工实践，我们总结出下面四个方面是研究混凝土浇筑技术的基础：第一，合理选择混凝土材料；第二，采用恰当的混凝土浇筑方式；第三，合理确定混凝土配合比例；第四，加强混凝土的温度控制及其养护。
2.1混凝土材料的选取应以遵循设计要求与规范为基础
第一，为更好地防止混凝土温度升高，需要采用低熱或中热水泥，从而可以使混凝土的温度应力符合相关要求。若建筑施工中选择强度等级合理的由某些成分组成的水泥材料，可以使其水化热得到有效控制，从而使得大体积混凝土温度升高的范围合理。第二，可以把一定量的粉煤灰放入混凝土。如果放入的粉煤灰量合理，其量为水泥量的三分之一至二分之一，如此方可更好地应用粉煤灰的某些性质，也就是所谓的滚球效应，这可以不仅可以提高混凝土的流动性，而且还可以增强器粘结性，此外，对于其水化热的控制也具有良好的效果。与此同时，把一定量的粉煤灰加入混凝土中，如此可以减少水泥的使用量，从而节约了生产费用。第三，在混凝土中加入一定量的相关增强剂。如此能够使得混凝土的水灰比控制在一定的范围，防止其收缩过大，优化其孔结构，增大其拉应力，甚至还能够改善混凝土的抗裂性及其抗渗性。第四，充分发挥混凝土后期强度的作用。根据丰富的建筑施工经验可知，为得到很好的混凝土后期强度，需把一定量的性能极好的粉煤灰放入混凝土中，在满足合理地水灰比条件下，可以是混凝土形成一个极好的强度增长，故而，大体积混凝土施工过程中往往选择一些高龄期的粉煤灰，才能获得合理的强度，如此能够减少水泥的使用量，还能够使混凝土温升得到有效的控制。
2.2以合理的方式方法进行混凝土浇筑
现如今，在建筑工程作业中，往往选择砖模或木模，以使得大体积混凝土外表的热挥发量降低。如果选择钢模的话，应注意其热挥发量的特殊情况，有可能造成混凝土表里存有较大的温差，因此，应选择相应的保温方法。进行大体积混凝土浇筑施工时，可按全过程设计要求，结合混凝土的相关特点，选择斜分层等形式，使混凝土厚度逐渐增加。
2.3合理确定混凝土配制比
合理的混凝土配制比可以使大体积混凝土的质量得到很好地提升。下面几个举措均可提高混凝土质量：合理确定水和水泥的量比，使得含泥量满足一定的范围，确定合理的骨料级配，提出相关方案，还需使得钢筋等不出现变动。在建筑施工中，往往使用泵送方式进行大体积混凝土浇筑，所以，合理确定配制比应满足减少水泥使用量和浇筑方法的要求。睡你的使用量不宜过多或过少，应确定在合理的范围。同时，砂率也应保证有合理的范围，应使石子的级配符合一定的要求。
2.4加强温控和养护数据搜集工作
处理好大体积混凝土的养护工作需要使混凝土的温度和湿度满足一定的要求，因此，应选择相关保温方法，以降低混凝土外部的热量挥发，减少其表里的温度差值，从而避免其产生裂缝。为使其温度得到更好地控制，需要选择科学的测温方法，这一工作应养护中做好，在混凝土浇筑工作结束后，就立即对其进行养护，其温度测量有两种方法，一是人工方法；二是计算机方法。此二种方可以同时使用在建筑施工中，也可任选一种。要视实际情况而定。
结束语
综上所述，进行好大体积混凝土浇筑施工绝非一项简单的事情，可谓是一个伟大的工程。在建筑施工中，对其质量产生不利影响的原因多不堪言，如果浇筑技术应用得不当，混凝土往往会存有较为严重的质量问题。故而，为使得大体积混凝土浇筑施工不受混凝土质量中出现的问题的影响，应找到合理的浇筑技术方法，以保证混凝土施工质量，从而获得较好的建筑施工质量。
参考文献
[1] 陈寰.对建筑施工中的混凝土浇筑技术探讨[J].价值工程,2011(03)
[2] 邓小钱.建筑施工中的大体积混凝土浇筑技术[J].中国水运(下半月),2009(03)
[3] 周安明,陈斌.对混凝土浇筑技术的探讨 [J].中国新技术新产品,2010(22)
[4] 李丽宏.“三掺技术”在大体积混凝土施工中的应用.民营科技.2008（02）
[5] 江正荣.建筑施工工程师手册［M］.北京：中国建筑工业出版社，2002（12）
[6] 孙修艾、程曙明.大面积框架结构梁板混凝土一次整体浇筑施工技术[J].建筑技术，2003（01）
[7] 李国胜.建筑结构裂缝及加固疑难问题的处理——附实例[M].北京：中国建筑工业出版社，2006.
[8] 迟陪云.大体积混凝土裂缝的起因及防治措施[J].混凝土，2001（12）
[9] 陈勇.混凝土浇筑技术措施[J].大众科技,2011(08)