【摘 要】
：
Fabrication of ternary Nb-17Si-23Ti alloys was attempted by in situ reaction laser melting deposition (LMD) with dual powder feeding method from Nb-28 at.％ Ti powder mixture and pure Si powder.The microstructures of the asdeposited alloys were examined wi
【机 构】
：
3D Printing Research and Engineering Technology Center,Beijing Institute of Aeronautical Materials,
论文部分内容阅读
Fabrication of ternary Nb-17Si-23Ti alloys was attempted by in situ reaction laser melting deposition (LMD) with dual powder feeding method from Nb-28 at.％ Ti powder mixture and pure Si powder.The microstructures of the asdeposited alloys were examined with scanning electronic microscope,and the phase constituents were analyzed by X-ray energy-dispersive spectrometer and X-ray diffraction.Furthermore,the effect of laser power on microstructure characteristics,microhardness and indentation fracture toughness was also investigated.The in situ reaction LMD process resulted in remarkable refinement of the microstructure.The as-deposited samples mainly consisted of Nbss,metastable (NbTi)3Si and Ti-rich Nbss.With the increase in the laser power from 1000 to 2000 W,the Nbss morphology changed from discontinuous dendritic to near equiaxed,but the Ti-rich Nbss phase tended to vanish.Furthermore,with the increase in the laser power,the microhardness of as-deposited samples increased from 822 to 951 HV,while the indentation fracture toughness was improved from 12.3 to 14.1 MPa m1/2.The corresponding mechanism is also discussed.
其他文献
The precipitation kinetics of σ phase in commercial HR3C heat-resistant steel during aging at 650-800 ℃ was studied in the paper.Through morphology,composition and structural analyzing on the second phase in the HR3C steel,it was confirmed that the precip
Using the flow stress curves obtained by Gleeble thermo-mechanical testing,the processing map of extruded magnesium alloy AZ31 was established to analyze the hot workability.Stress exponent and activation energy were calculated to characterize the deforma
In the present study,the effect of Zn content on the microstructure and deformation behavior of the as-cast Mg-Zn-Y-Nd alloy has been investigated.The results showed that as Zn content increased,the volume fraction of secondary phases increased.Moreover,t
It has been recently pointed out that the compositions of industrial alloys are originated from cluster-plus-glueatom structure units in solid solutions.Specifically for Ni-based superalloys,after properly grouping the alloying elements into Al,Ni-like (N
Workability domain without the onset of flow instability was developed by numerical simulation and response surface method (RSM) for complex-shaped straight spur gear forging.The processing map of AZ31B alloys was calculated from flow stress curves and th
In the present study,a novel bacterium (Marinobacter aquaeolei) was examined for its corrosion inhibiting behaviour against X80 pipeline steel.Electrochemical results showed that X80 steel immersed in the solution inoculated with M.aquaeolei possessed ver
This study investigated the microstructure,mechanical,and damping properties of a non-age-hardened Al alloy (5086) and an age-hardened Al alloy (7075) after friction stir processing (FSP).Microstructural analyses indicate that FSP led the grain refinement
The as-cast microstructure,element segregation and solidification behavior of a multi-alloyed superalloy ЭК151 have been investigated.The results show that the severe element segregation leads to the complicated precipitations at the inter-dendritic regio
The pure Zn foils with different thicknesses (0.02,0.05,0.1,0.2 and 0.3 mm) were selected as interlayers to improve the quality of friction stir lap welding joint of 7075-T6 Al and AZ31B Mg dissimilar alloys.The effects of the interlayer thickness on join