【摘 要】
：
本文研究了在２０％Ｈ２ＳＯ４溶液中奥氐体不锈钢焊接接头的腐蚀行为。结果指 出．焊接材料的热影响区对腐蚀较为敏感，其腐蚀形态多呈晶间腐蚀．原因在于，受 焊接的热影响，晶界沉淀析出碳化物，导致晶
【机 构】
：
大连工学院腐蚀与防护教研室,大连工学院腐蚀与防护教研室,大连工学院腐蚀与防护教研室
论文部分内容阅读
本文研究了在２０％Ｈ２ＳＯ４溶液中奥氐体不锈钢焊接接头的腐蚀行为。结果指 出．焊接材料的热影响区对腐蚀较为敏感，其腐蚀形态多呈晶间腐蚀．原因在于，受 焊接的热影响，晶界沉淀析出碳化物，导致晶界处发生选择性腐蚀。同时，还模拟了 晶界贫铬区，进行了一系列电化学试验，探讨了贫铬区的再活化溶解行为。
In this paper, the corrosion behavior of austenitic stainless steel welded joint in 20% H2SO4 solution was studied. The results indicate. The heat-affected zone of the welding material is more sensitive to corrosion, and the corrosion morphology is mostly intergranular corrosion. The reason is that by the heat of welding, the grain boundary precipitates carbides, resulting in selective corrosion at the grain boundaries. At the same time, a series of electrochemical tests were also carried out to simulate the chromium-depleted zone in the grain boundary, and the reactivation dissolution behavior in the depleted zone was also discussed.
其他文献
一、引言液压机和压力机组合式机架、立柱需要预紧,板材和管材矫直机的机架、立柱也需要预紧,其他类似的结构也有预紧的问题。这类设备机架、立柱预紧的质量如何,将直接关系
2007年,青岛市提出了以村庄的“硬化、亮化、绿化、净化、美化”为重点的新农村建设“五化”目标。近年来特别是去年以来,青岛市各级林业部门加大了村庄绿化、美化步伐,如今
序言火力发电用锅炉汽包、各类化工设备中的反应容器及用核电压力壳等,所有这些压力容器在近代工业的各个领域中,作为极其重要的设备之一得到了广泛的运用。容器的结构、材
加快农村电影改革发展,努力让广大农民群众看到、看好电影,对于在农村宣传党的路线方针政策,普及科学技术知识,发展农村先进文化,提高农民的思想道德、科学文化和身体健康素
材料的切削加工性和其机械性能有关,即材料的硬度、强度、塑性、韧性以及弹性都能影响材料的切削加工性。而材料的机械性能往往是随温度的升降而变化的。通常,温度升高时,材
本文对大面积工件电镀高质量耐磨硬铬工艺作了研究,发现影响镀层质量的因素基本有二:(1)基体表面是否存在凹形缺陷,及造成这种缺陷的原因是电镀前处理过程中,酸浸活化及阳极
本刊被确定为综合性轻工类的核心期刊本刊主编孙凤翔同志于今年７月收到《中文核心期刊要目总览》第二版编委会的书面通知。通知中说，依据文献计量学的原理和方法，经过研究人员对
我国的经济改革如何进一步深入,是社会各个阶层都在积极思考的问题。本文的着眼点不在于具体的对策性意见,而是就目前人们议论较多、也是对改革的进程影响较大的三个问题发
车轴是机车车辆走行部分最重要的零件之一。在运转过程中,它要承受复杂的交变负荷,工况十分恶劣。因此,在车轴的制造、装配和使用过程中,任何质量上的疏忽都将会招致不堪设
轧辊是轧钢生产设备的关键部件,它费用高,消耗量大,因此,在如何延长它的使用寿命和修复废旧轧辊方面,国内外正进行大量的研究工作。目前,用堆焊技
Roll is a key part of r