论文部分内容阅读
Microstructure and subsequent phase transformations on heating of the melt-spun Nd85Al15 alloy have been studied by X-ray diffraction, transmission electron microscopy and differential scanning calorimetry. The melt-spun Nd85Al15 alloy shows two-stage transformation processes as follows: amorphous+72 nm supersaturated bcc-Nd(AI) solid solution-7 nm omega-like phase-AlNd3+hexagonal Nd. The activation energies for the first and second transformation were found to be 100 kJ/mol and 188 kJ/mol, respectively. The formation mechanism of nanoscale omega-like phase is discussed.
Microstructure and subsequent phase transformations on heating of the melt-spun Nd85Al15 alloy have been studied by X-ray diffraction, transmission electron microscopy and differential scanning calorimetry. The melt-spun Nd85Al15 alloy shows two-stage transformation processes as follows: amorphous + 72 nm The activation energies for the first and second transformation were found to be 100 kJ / mol and 188 kJ / mol, respectively. The formation mechanism of supersaturated bcc-Nd (AI) solid solution-7 nm omega-like phase-AlNd3 + hexagonal Nd. of nanoscale omega-like phase is discussed.