标题化合物采用锌粉、硫粉及２－甲基吡啶直接反应最后得到金黄色晶体，其具有萤光性能，它不溶于水及二硫化碳．进行Ｘ－射线结晶学表征，该分子中含有四面体配位的ＺｎＳ２Ｎ２核心．结晶学参数：单斜晶系，ＣＣ，Ｚ＝４，ａ＝０．７５１３６（２４）ｎｍ，ｂ＝１．７３０６５（７９）ｎｍ，ｃ＝１．３６８１２（３７）ｎｍ，α＝９０．０１８°（３０），β＝９４．４４９°（２７），γ＝８９．９４７°（４２），Ｖ＝１．７７３６６ｎｍ３．通过元素分析其化学式为ＺｎＳ６（Ｃ６Ｈ７Ｎ）２．对标题化合物进行红外光谱归属，同时进行热分析，循环伏安以及荧光性能的研究，发现温度大于１０４℃时开始分解，于３８０℃全部分解，最后产物为ＺｎＳ
The title compound was directly reacted with zinc powder, sulfur powder and 2-methylpyridine to finally give a golden yellow crystal, which has a fluorescent property and is insoluble in water and carbon disulfide. X-ray crystallographic characterization of the tetrahedral coordinated ZnS2N2 core. Crystallographic parameters: monoclinic, CC, Z = 4, a = 0.75136 (24) nm, b = 1.73065 (79) nm, c = 1.36812 (37) nm, ° (30), β = 94.449 ° (27), γ = 89.947 ° (42), V = 1.77366 nm3. Its chemical formula is ZnS6 (C6H7N) 2 by elemental analysis. At the same time, the thermal analysis, cyclic voltammetry and fluorescence properties of the title compounds were studied. It was found that when the temperature was above 104 ℃, they began to decompose and decomposed at 380 ℃. The final product was ZnS