【摘 要】水工混凝土缺陷处理是一项复杂而细致的工作。在混凝土缺陷处理之前，首先要进行详细的调查，分析混凝土产生缺陷的原因，有的放矢地制定处理方案。同时，要有一支专业施工队伍，施工前要做出合理的施工组织设计，施工中要有熟练的施工技术人员进行操作。在施工过程中，有时还要根据工程具体情况对施工工艺做必要的修改，以保证施工方案的实施。
【关键词】混凝土缺陷；处理
Common defects and hydraulic concrete processing method
Zhao Xiao-na
(Xinjiang yili River Basin Development and Construction Autho Yining Xinjiang 835000)
【Abstract】Hydraulic concrete defect treatment is a complex and painstaking work. Defects in the concrete before processing, the first detailed investigation, analysis of the causes of concrete defects, development of targeted treatment programs. At the same time, there must be a professional construction team to make a reasonable pre-construction construction design, construction and technical personnel should be trained to operate construction. During the construction process, sometimes under the specific circumstances of the construction process works to make the necessary changes to ensure the implementation of the construction program.
【Key words】Concrete defects;Treatment
1. 引言
水利工程通常都由很多的混凝土建筑物、构筑物构成结构主体，因此混凝土质量的好坏对水利枢纽的顺利、安全运行有重要的影响。但是由于各种原因，混凝土往往存在着各种缺陷，为了保证结构的质量，就必须对这些混凝土缺陷进行处理。
2. 常见混凝土缺陷形成原因、预防措施以及处理方法
2.1 砼麻面。
2.1.1 现象：砼表面局部缺浆粗糙，或有许多小凹坑，但无钢筋和碎石外露。
2.1.2 原因分析：模板表面粗糙或清理不干净，粘有干硬水泥砂浆等杂物，拆模时砼表面被粘损；钢模板脱模剂涂刷不均匀，拆模时砼表面粘结模板；模板接缝拼装不严密，灌注砼时缝隙漏浆；砼振捣不密实，砼中的气泡未排出，一部分气泡停留在模板表面。
2.1.3 预防措施： 模板面清理干净，不得粘有干硬水泥砂浆等杂物。木模板灌注砼前，用清水充分湿润，清洗干净，不留积水，使模板缝隙拼接严密，如有缝隙，填严，防止漏浆。钢模板涂模剂要涂刷均匀，不得漏刷。砼必须按操作规程分层均匀振捣密实，严防漏捣，每层砼均匀振捣至气泡排除为止。
2.1.4 处理方法：麻面主要影响砼外观，对于面积较大的部位修补。即将麻面部位用清水刷洗，充分湿润后用潮湿的水泥抹平。
2.2 蜂窝。
2.2.1 现象：砼局部酥松，砂浆少碎石多，碎石之间出现空隙，形成蜂窝状的孔洞。
2.2.2 原因分析：模板表面油性隔离剂配制过稠、涂抹过多，致使拌和料人仓振捣时，隔离剂在表面张力的作用下，沿接触模板的混合料表面出现浸润现象，并包裹其内的气体形成气泡。此部分气泡在振捣过程中大多逐渐溢出并变小，剩余部分因油性隔离剂的黏稠度较高而继续吸附于模板表面，较难溢出仓外的气泡，在混凝土凝结后形成气泡空隙；浇筑层厚度过大，气泡的溢出行程过长，也易引起气泡偏多的现象。
2.2.3 预防措施：采用稀释剂(如柴油等)，降低隔离剂稠度，相应减少封闭气泡的吸附力；减小涂抹厚度，并以润湿模板表面为宜，由此减少浸润气泡数量及浸润膜厚度，便于其内气体在振捣时破膜而出；适当延长模板附近振点的振捣时间，以帮助此类气泡溢出；调减浇筑层厚度，以缩短模板表面气泡的溢出行程；使用适量的减水剂，增大和易性，提高气泡的振升速率。
2.2.4 治理方法：砼有小蜂窝，可先用水冲洗干净，然后用1∶2或1∶2.5水泥砂浆修补，如果是大蜂窝，则先将松动的碎石和突出颗粒剔除，尽量形成喇叭口，外口大些，然后用清水冲洗干净湿润，再用高一级的细石砼捣实，加强养护。
2.3 孔洞。
2.3.1 现象：砼结构内有空隙，局部没有砼。
2.3.2 原因分析：在钢筋密集处或预埋件处，砼浇注不畅通，不能充满模板间隙；未按顺序振捣砼，产生漏振；砼离析，或严重跑浆；砼工程的施工组织不好，未按施工顺序和施工工艺认真操作；砼中有硬块和杂物掺入，或木块等大件料具掉入砼中；不按规定下料，一次下料过多，下部因振捣器振动作用半径达不到，形成松散状态。
2.3.3 预防措施：
（1）在钢筋密集处，可采用细石砼浇注，使砼充满模板间隙，并认真振捣密实。
（2）预留孔洞处在两侧同时下料。
（3）采用正确的振捣方法，严防漏振。
（4）控制好下料。要保证砼灌注时不产生离析，砼自由倾落高度不超过2m。
（5）防止砂、石中混有粘土块或冰块等杂物，发现砼中有杂物，及时清除干净。
（6）加强施工技术管理和质量检查工作。
2.3.4 对砼孔洞的处理，要经有关单位共同研究，制定补强方案，经批准后方可处理。
2.4 露筋。
2.4.1 现象：钢筋砼结构内的钢筋露在砼表面。
2.4.2 原因分析：砼浇注振捣时，钢筋垫块移位或垫块太少甚至漏放，钢筋紧贴模板；钢筋砼结构断面较小，钢筋过密，如遇粒径大碎石卡在钢筋上，砼水泥浆不能充满钢筋周围；因配合比不当砼产生离析，或模板严重漏浆；砼振捣时，振捣棒撞击钢筋，使钢筋移位；砼保护层振捣不密实，或木模板湿润不够，砼表面失水过多，或拆模过早等，拆模时砼缺棱掉角。
2.4.3 预防措施：
（1）灌注砼前，检查钢筋位置和保护层厚度是否准确。
（2）为保证砼保护层的厚度，要注意固定好垫块。
（3）钢筋较密集时，选配适当粒径的碎石。碎石最大粒径不得超过结构截面最小尺寸的1/4，同时不得大于钢筋净距的3/4。结构截面较小，钢筋较密时，可用细石砼浇注。
（4）操作时不得踩踏钢筋，如钢筋有踩弯或脱扣者，及时调直，补扣绑好。
2.4.4 治理方法：将外露钢筋上的砼残渣和铁锈清理干净，用水冲洗湿润，再用 1∶2或1∶2.5水泥砂浆抹压平整，如露筋较深，将薄弱砼剔除，冲刷干净湿润，用高一级的细石砼捣实，认真养护。
2.5 缺棱掉角。
2.5.1 现象：砼局部掉落，不规整，棱角有缺陷。
2.5.2 原因分析：木模板在浇注砼前未湿润或湿润不够，灌注后砼养护不好，棱角处砼的水分被模板大量吸收，致使砼水化不好，强度降低；施工时，过早拆除承重模板；拆模时受外力作用或重物撞击，或保护不好，棱角被碰掉；冬季施工时，砼局部受冻。
2.5.3 预防措施：木模板在灌注砼前充分湿润，砼浇注后认真浇水养护。拆除钢筋砼结构承重模板时，砼具有足够的强度，表面及棱角才不会受到损坏。拆模时不能用力过猛过急，注意保护棱角，吊运时，严禁模板撞击棱角。加强成品保护，对于处在人多、运料等通道处的砼阳角，拆模后可用槽钢等将阳角保护好，以免碰损。冬季砼浇注完毕，做好覆盖保温工作，加强测温，及时采取措施，防止受冻。
2.5.4 治理方法：缺棱掉角较小时，，清水冲洗可将该处用钢丝刷刷净充分湿润后，用1∶2或1∶2.5的水泥砂浆抹补齐正。可将不实的砼和突出的骨料颗粒凿除，用水冲刷干净湿润，然后用比原砼高一级的细石砼补好，认真养护。
2.6 施工缝夹层。
2.6.1 现象：施工缝处砼结合不好，有缝隙或夹有杂物，造成结构整体性不良。
2.6.2 原因分析：在灌注砼前没有认真处理施工缝表面，浇注前，捣实不够；灌注大体积砼结构时，往往分层分段施工。在施工停歇期间常有木块、锯末等杂物积存在砼表面，未认真检查清理，再次灌注砼时混入砼内，在施工缝处造成杂物夹层 。
2.6.3 预防措施：
（1）在施工缝处继续灌注砼时，如间歇时间超过规定，则按施工缝处理，在砼抗压强度不小于1.2Mpa时，才允许继续灌注。
（2）在已硬化的砼表面上继续灌注砼前，除掉表面水泥薄膜和松动碎石或软弱砼层，并充分湿润和冲洗干净，残留在砼表面的水予清除。
（3）在浇注前，施工缝宜先铺抹水泥浆一层。
2.6.4 治理方法：当表面缝隙较细时，可用清水将裂缝冲洗干净，充分湿润后抹水泥浆。对夹层的处理慎重。补强前，先搭临时支撑加固后，方可进行剔凿。将夹层中的杂物和松软砼清除，用清水冲洗干净，充分湿润，再灌注，采用提高一级强度等级的细石砼捣实并认真养护。
3. 常见修补材料及工艺
3.1 麻布擦抹法 首先表面要充分湿润。用干净的麻布或橡胶海绵抹子在整个表面上擦抹砂浆，以填满所有的气孔和凹坑：所用的砂浆配比为1份水泥和2份砂，砂的最大尺寸小于600μm，砂浆用水量要足以使其稠度成为浓乳浆。开始擦抹前24小时，应采取遮蔽或喷雾的方法，保持待补表面局部周围环境温度不超过10℃。
当凹坑内的砂浆还具有塑性时，在表面上撒一层水泥和砂的干拌物后再打磨，配比与前述相同。
3.2 干填砂浆 干填砂浆为分层填筑：修补材料拌和物由1份水泥和2.5份砂(级配为100%通过1.18mm筛)组成。适量加水，使产生的砂浆用手稍加力捏，能粘在一起，手变潮但不湿。干填前要浸泡待补面，等其处于饱和面干状态时开始填筑：干填时每10mm一层用木锤进行夯实。然后刮平至与周围表而平齐。
3.3 环氧和聚合物 各种环氧和聚合物类修补材料，可遵照供货厂家的工艺和配比要求进行施工。
4. 外观质量控制中其他几点相关事项
4.1 表面施工滞留物的清除及孔眼的封堵、修补。
对施工过程中可能滞留于混凝土中而无法拔出的拉杆、撑件等必须予以割除，后与孔眼一起进行封堵、修补；同时，为减小色差，建议在进行连接层处理后，用原施工配合比及各类组料拌制混凝土修补。
4.2 混凝土成型构件的维护。
构件成型后，必须进行维护。拆模过程中，应将模板沿接缝逐一取出，避免硬敲引起成型构件碰损、掉角；拆模后的结构物，不得作为物品的集放处及其他构件的架模支撑点，不得让油渍、砂浆等杂物飞溅、挂溢其上。同样，应做好工程运行管理阶段的维护工作。
4.3 钢筋保护层的控制。
保护层过大，钢筋达不到设计受力状态，温度筋远离层面，表面易开裂；过小，则耐久性下降，常常在工程投入运行后的一定时间内，引起内部钢筋失钝锈蚀而膨胀，导致表层混凝土沿钢筋方向的爆裂、松脱。保护层控制不当，有时还会形成露筋，严重影响构件受力及外观。
5. 结语
水工混凝土缺陷处理是一项复杂而细致的工作。在混凝土缺陷处理之前，首先要进行详细的调查，分析混凝土产生缺陷的原因，有的放矢地制定处理方案。同时，要有一支专业施工队伍，施工前要做出合理的施工组织设计，施工中要有熟练的施工技术人员进行操作。在施工过程中，有时还要根据工程具体情况对施工工艺做必要的修改，以保证施工方案的实施。
［文章编号］1006-7619（2011）05-25-590
【关键词】混凝土缺陷；处理
Common defects and hydraulic concrete processing method
Zhao Xiao-na
(Xinjiang yili River Basin Development and Construction Autho Yining Xinjiang 835000)
【Abstract】Hydraulic concrete defect treatment is a complex and painstaking work. Defects in the concrete before processing, the first detailed investigation, analysis of the causes of concrete defects, development of targeted treatment programs. At the same time, there must be a professional construction team to make a reasonable pre-construction construction design, construction and technical personnel should be trained to operate construction. During the construction process, sometimes under the specific circumstances of the construction process works to make the necessary changes to ensure the implementation of the construction program.
【Key words】Concrete defects;Treatment
1. 引言
水利工程通常都由很多的混凝土建筑物、构筑物构成结构主体，因此混凝土质量的好坏对水利枢纽的顺利、安全运行有重要的影响。但是由于各种原因，混凝土往往存在着各种缺陷，为了保证结构的质量，就必须对这些混凝土缺陷进行处理。
2. 常见混凝土缺陷形成原因、预防措施以及处理方法
2.1 砼麻面。
2.1.1 现象：砼表面局部缺浆粗糙，或有许多小凹坑，但无钢筋和碎石外露。
2.1.2 原因分析：模板表面粗糙或清理不干净，粘有干硬水泥砂浆等杂物，拆模时砼表面被粘损；钢模板脱模剂涂刷不均匀，拆模时砼表面粘结模板；模板接缝拼装不严密，灌注砼时缝隙漏浆；砼振捣不密实，砼中的气泡未排出，一部分气泡停留在模板表面。
2.1.3 预防措施： 模板面清理干净，不得粘有干硬水泥砂浆等杂物。木模板灌注砼前，用清水充分湿润，清洗干净，不留积水，使模板缝隙拼接严密，如有缝隙，填严，防止漏浆。钢模板涂模剂要涂刷均匀，不得漏刷。砼必须按操作规程分层均匀振捣密实，严防漏捣，每层砼均匀振捣至气泡排除为止。
2.1.4 处理方法：麻面主要影响砼外观，对于面积较大的部位修补。即将麻面部位用清水刷洗，充分湿润后用潮湿的水泥抹平。
2.2 蜂窝。
2.2.1 现象：砼局部酥松，砂浆少碎石多，碎石之间出现空隙，形成蜂窝状的孔洞。
2.2.2 原因分析：模板表面油性隔离剂配制过稠、涂抹过多，致使拌和料人仓振捣时，隔离剂在表面张力的作用下，沿接触模板的混合料表面出现浸润现象，并包裹其内的气体形成气泡。此部分气泡在振捣过程中大多逐渐溢出并变小，剩余部分因油性隔离剂的黏稠度较高而继续吸附于模板表面，较难溢出仓外的气泡，在混凝土凝结后形成气泡空隙；浇筑层厚度过大，气泡的溢出行程过长，也易引起气泡偏多的现象。
2.2.3 预防措施：采用稀释剂(如柴油等)，降低隔离剂稠度，相应减少封闭气泡的吸附力；减小涂抹厚度，并以润湿模板表面为宜，由此减少浸润气泡数量及浸润膜厚度，便于其内气体在振捣时破膜而出；适当延长模板附近振点的振捣时间，以帮助此类气泡溢出；调减浇筑层厚度，以缩短模板表面气泡的溢出行程；使用适量的减水剂，增大和易性，提高气泡的振升速率。
2.2.4 治理方法：砼有小蜂窝，可先用水冲洗干净，然后用1∶2或1∶2.5水泥砂浆修补，如果是大蜂窝，则先将松动的碎石和突出颗粒剔除，尽量形成喇叭口，外口大些，然后用清水冲洗干净湿润，再用高一级的细石砼捣实，加强养护。
2.3 孔洞。
2.3.1 现象：砼结构内有空隙，局部没有砼。
2.3.2 原因分析：在钢筋密集处或预埋件处，砼浇注不畅通，不能充满模板间隙；未按顺序振捣砼，产生漏振；砼离析，或严重跑浆；砼工程的施工组织不好，未按施工顺序和施工工艺认真操作；砼中有硬块和杂物掺入，或木块等大件料具掉入砼中；不按规定下料，一次下料过多，下部因振捣器振动作用半径达不到，形成松散状态。
2.3.3 预防措施：
（1）在钢筋密集处，可采用细石砼浇注，使砼充满模板间隙，并认真振捣密实。
（2）预留孔洞处在两侧同时下料。
（3）采用正确的振捣方法，严防漏振。
（4）控制好下料。要保证砼灌注时不产生离析，砼自由倾落高度不超过2m。
（5）防止砂、石中混有粘土块或冰块等杂物，发现砼中有杂物，及时清除干净。
（6）加强施工技术管理和质量检查工作。
2.3.4 对砼孔洞的处理，要经有关单位共同研究，制定补强方案，经批准后方可处理。
2.4 露筋。
2.4.1 现象：钢筋砼结构内的钢筋露在砼表面。
2.4.2 原因分析：砼浇注振捣时，钢筋垫块移位或垫块太少甚至漏放，钢筋紧贴模板；钢筋砼结构断面较小，钢筋过密，如遇粒径大碎石卡在钢筋上，砼水泥浆不能充满钢筋周围；因配合比不当砼产生离析，或模板严重漏浆；砼振捣时，振捣棒撞击钢筋，使钢筋移位；砼保护层振捣不密实，或木模板湿润不够，砼表面失水过多，或拆模过早等，拆模时砼缺棱掉角。
2.4.3 预防措施：
（1）灌注砼前，检查钢筋位置和保护层厚度是否准确。
（2）为保证砼保护层的厚度，要注意固定好垫块。
（3）钢筋较密集时，选配适当粒径的碎石。碎石最大粒径不得超过结构截面最小尺寸的1/4，同时不得大于钢筋净距的3/4。结构截面较小，钢筋较密时，可用细石砼浇注。
（4）操作时不得踩踏钢筋，如钢筋有踩弯或脱扣者，及时调直，补扣绑好。
2.4.4 治理方法：将外露钢筋上的砼残渣和铁锈清理干净，用水冲洗湿润，再用 1∶2或1∶2.5水泥砂浆抹压平整，如露筋较深，将薄弱砼剔除，冲刷干净湿润，用高一级的细石砼捣实，认真养护。
2.5 缺棱掉角。
2.5.1 现象：砼局部掉落，不规整，棱角有缺陷。
2.5.2 原因分析：木模板在浇注砼前未湿润或湿润不够，灌注后砼养护不好，棱角处砼的水分被模板大量吸收，致使砼水化不好，强度降低；施工时，过早拆除承重模板；拆模时受外力作用或重物撞击，或保护不好，棱角被碰掉；冬季施工时，砼局部受冻。
2.5.3 预防措施：木模板在灌注砼前充分湿润，砼浇注后认真浇水养护。拆除钢筋砼结构承重模板时，砼具有足够的强度，表面及棱角才不会受到损坏。拆模时不能用力过猛过急，注意保护棱角，吊运时，严禁模板撞击棱角。加强成品保护，对于处在人多、运料等通道处的砼阳角，拆模后可用槽钢等将阳角保护好，以免碰损。冬季砼浇注完毕，做好覆盖保温工作，加强测温，及时采取措施，防止受冻。
2.5.4 治理方法：缺棱掉角较小时，，清水冲洗可将该处用钢丝刷刷净充分湿润后，用1∶2或1∶2.5的水泥砂浆抹补齐正。可将不实的砼和突出的骨料颗粒凿除，用水冲刷干净湿润，然后用比原砼高一级的细石砼补好，认真养护。
2.6 施工缝夹层。
2.6.1 现象：施工缝处砼结合不好，有缝隙或夹有杂物，造成结构整体性不良。
2.6.2 原因分析：在灌注砼前没有认真处理施工缝表面，浇注前，捣实不够；灌注大体积砼结构时，往往分层分段施工。在施工停歇期间常有木块、锯末等杂物积存在砼表面，未认真检查清理，再次灌注砼时混入砼内，在施工缝处造成杂物夹层 。
2.6.3 预防措施：
（1）在施工缝处继续灌注砼时，如间歇时间超过规定，则按施工缝处理，在砼抗压强度不小于1.2Mpa时，才允许继续灌注。
（2）在已硬化的砼表面上继续灌注砼前，除掉表面水泥薄膜和松动碎石或软弱砼层，并充分湿润和冲洗干净，残留在砼表面的水予清除。
（3）在浇注前，施工缝宜先铺抹水泥浆一层。
2.6.4 治理方法：当表面缝隙较细时，可用清水将裂缝冲洗干净，充分湿润后抹水泥浆。对夹层的处理慎重。补强前，先搭临时支撑加固后，方可进行剔凿。将夹层中的杂物和松软砼清除，用清水冲洗干净，充分湿润，再灌注，采用提高一级强度等级的细石砼捣实并认真养护。
3. 常见修补材料及工艺
3.1 麻布擦抹法 首先表面要充分湿润。用干净的麻布或橡胶海绵抹子在整个表面上擦抹砂浆，以填满所有的气孔和凹坑：所用的砂浆配比为1份水泥和2份砂，砂的最大尺寸小于600μm，砂浆用水量要足以使其稠度成为浓乳浆。开始擦抹前24小时，应采取遮蔽或喷雾的方法，保持待补表面局部周围环境温度不超过10℃。
当凹坑内的砂浆还具有塑性时，在表面上撒一层水泥和砂的干拌物后再打磨，配比与前述相同。
3.2 干填砂浆 干填砂浆为分层填筑：修补材料拌和物由1份水泥和2.5份砂(级配为100%通过1.18mm筛)组成。适量加水，使产生的砂浆用手稍加力捏，能粘在一起，手变潮但不湿。干填前要浸泡待补面，等其处于饱和面干状态时开始填筑：干填时每10mm一层用木锤进行夯实。然后刮平至与周围表而平齐。
3.3 环氧和聚合物 各种环氧和聚合物类修补材料，可遵照供货厂家的工艺和配比要求进行施工。
4. 外观质量控制中其他几点相关事项
4.1 表面施工滞留物的清除及孔眼的封堵、修补。
对施工过程中可能滞留于混凝土中而无法拔出的拉杆、撑件等必须予以割除，后与孔眼一起进行封堵、修补；同时，为减小色差，建议在进行连接层处理后，用原施工配合比及各类组料拌制混凝土修补。
4.2 混凝土成型构件的维护。
构件成型后，必须进行维护。拆模过程中，应将模板沿接缝逐一取出，避免硬敲引起成型构件碰损、掉角；拆模后的结构物，不得作为物品的集放处及其他构件的架模支撑点，不得让油渍、砂浆等杂物飞溅、挂溢其上。同样，应做好工程运行管理阶段的维护工作。
4.3 钢筋保护层的控制。
保护层过大，钢筋达不到设计受力状态，温度筋远离层面，表面易开裂；过小，则耐久性下降，常常在工程投入运行后的一定时间内，引起内部钢筋失钝锈蚀而膨胀，导致表层混凝土沿钢筋方向的爆裂、松脱。保护层控制不当，有时还会形成露筋，严重影响构件受力及外观。
5. 结语
水工混凝土缺陷处理是一项复杂而细致的工作。在混凝土缺陷处理之前，首先要进行详细的调查，分析混凝土产生缺陷的原因，有的放矢地制定处理方案。同时，要有一支专业施工队伍，施工前要做出合理的施工组织设计，施工中要有熟练的施工技术人员进行操作。在施工过程中，有时还要根据工程具体情况对施工工艺做必要的修改，以保证施工方案的实施。