The effect of surface gradient nanostructure on the fatigue life of commercial pure (CP) Zr was inves-tigated.Four point bending fatigue tests indicated that the fatigue limit of CP Zr with surface gradient nanostructure was increased by about 28.3 ％ comp
【机 构】
：
School of Metallurgical Engineering,Xi’an University of Architecture and Technology,Xi’an,710055,Chi
论文部分内容阅读
The effect of surface gradient nanostructure on the fatigue life of commercial pure (CP) Zr was inves-tigated.Four point bending fatigue tests indicated that the fatigue limit of CP Zr with surface gradient nanostructure was increased by about 28.3 ％ compared with the original sample (annealed state).The microstructure evolution at different fatigue loading stages was characterized.The high strength of sur-face gradient nanostructure could increase the crack initiation resistance.Furthermore,electron back scattered diffraction (EBSD) analysis demonstrated that the surface nanocrystals grew and rotated grad-ually during the fatigue loading,which was beneficial to reducing stress concentration,inhibit fatigue crack initiation,and prolong crack initiation life.The stored distortion energy of CP Zr calculated before and after fatigue indicated that the stored distortion energy decreased dramatically during cyclic load-ing,which provided the driving force for grain growth.Besides,the growth of nanocrystals consumed the mechanical energy produced by the applied load to a certain extent,thus,slowing down the accumulation of fatigue damage.The coarse grains at the interior could deform plastically and reduce the crack growth rate.In addition,the compressive residual stress caused by USSP treatment reduced the local effective stress and the driving force of crack growth.
其他文献
为探究考虑扰动效应时透水管桩桩周土的固结特性,利用有限元分析软件,建立了考虑扰动效应的饱和软黏土中透水管桩地基土固结三维模型,然后采用模型退化及试验实测数据对比两种方式进行有限元模拟准确性的验证.最后,在考虑扰动效应影响下,对不同开孔几何参数下桩周土超静孔压的消散情况进行了讨论.结果表明:模型退化验证及对比实测数据均与数值模拟结果基本保持一致,很好地验证了数值模拟的准确性;扰动程度系数α的变化仅对超静孔压前期的消散速率影响显著,并造成一定程度的孔压消散差,随着孔压消散的进行这一差距逐渐减小.扰动范围s的增
Both silicon and tin are promising anodes for new generation lithium ion batteries due to high lithium storage capacities (theoretically 4200 mA h g-1 and 992 mA h g-1,respectively).However,their large volumetric expansions (both are above 300 ％) usually
P-type semiconductivity has been observed in solid solution series (SrTiO3)1-x(CaCr0.5Nb0.5O3)x (0.0 ≤x ≤ 0.15),which all adopt cubic symmetry and own intense absorption in the visible light region.These solid solutions are superior H2 evolution photocata
1.IntroductionrnHigh strength steels continue to be developed for automotive applications to increase safety and reduce lightweight by down-gauging[1,2].In addition,reducing density is another solution for the lightweight of automotive components[3,4].Alu
The microstructure and room-temperature tensile deformation behavior of the cast CrFeCoNiAl0.7 high-entropy alloy (HEA) were studied in details.The cast HEA consisted of a dual-phase structure of 77.3 vol.％ face-centered-cubic (FCC) phase plus 22.7 vol.％
The top-down method was used to fabricate the TiNi1+xSn half-Heusler alloy.Several knotty problems have been solved using the top-down method,including the generation of impurity phases,the visi-ble discrepancy in the grain size of the TiNi2Sn second phas
The influence of different precipitate-dislocation interactions,namely dislocation shearing and bypass-ing mechanisms,on PLC bands and the resultant surface roughness in AlMgScZr alloy was investigated.Three-dimensional surface roughness was quantitativel
Low photothermal conversion efficiency restricts the antibacterial application of photothermal materials.In this work,two-dimensional carbon nanosheets (2D C) were prepared and decorated with Cu nanopar-ticles (2D C/Cu) by using a simple soluble salt temp
The electrochemical properties of a friction stir processed (FSPed) equiatomic CrMnFeCoNi high-entropy alloy (HEA) was investigated in an aerated 0.5 M Na2SO4 electrolyte solution at room temperature.The microstructural analysis reveals a highly refined s
The chain-like prior particle boundaries (PPBs) as a kind of stubborn harmful precipitate will hinder atomic diffusion and particle connection.They can only be broken into nanoscale through thermal defor-mation (1160-1200 ℃).Here,treated by the pulsed ele